Effect of internal nitridation on microstructure and mechanical properties of cobalt-based superalloy under high-temperature nitrogen atmosphere
Yipeng Chen,Yong Cai,Chao Yuan,Weiwen Kong,Yongqiang Wang,Xin Wen,Xin Liu
DOI: https://doi.org/10.1016/j.matchar.2023.112851
IF: 4.537
2023-04-01
Materials Characterization
Abstract:In this study, the microstructure and mechanical properties of cobalt-based superalloys by internal nitridation at 1100 °C, 1150 °C, and 1200 °C were characterised in detail by transmission electron microscope (TEM), electron probe microanalysis (EPMA), electron backscatter diffraction (EBSD) and microhardness testing. The results show that with an increase in the internal nitridation temperature, the nitridation layer thickness of cobalt-based superalloys gradually increases to 898 μm. Internal nitridation at 1200 °C for 10 h exhibits the densest nitrides and the thickest layer. The precipitates were then dispersed in the matrix. The precipitates are mainly cubic, spherical, and cruciform (Ti, Nb)(C, N). Small amounts of blocky AlN and Cr 2 N were observed in the outer nitridation layer. Internal nitridation significantly improves the mechanical properties of cobalt-based superalloys by precipitation and solution strengthening. The yield strength increased by 105% at room temperature (RT). Compared with the yield strength of 100 MPa for the as-received alloy at 800 °C, the internal nitridation alloy could still maintain good mechanical properties: a yield strength 300 MPa and an elongation 32%. In addition, because of the low diffusion activation energy of nitrogen in cobalt-based superalloys, internal nitridation is suitable for strengthening cobalt-based superalloys, expanding their application prospects in engineering structural materials.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing