Abstract:Cu/ZnO catalysts with varied Cu/(Cu + Zn) molar ratios were prepared by a facile solid-state method. The Cu/(Cu + Zn) molar ratio displayed a significant effect on the oxygen vacancy formation of the calcined catalysts, thereby influencing the CuO–ZnO interaction and the reducibility of CuO. The Cu/(Cu + Zn) molar ratio also exhibited a significant effect on Cu0 surface area, oxygen vacancy, the ratio of ZnO(002) plane to ZnO(100) plane, as well as the basicity and acidity of the reduced catalysts, thereby affecting the catalytic performance for low-temperature methanol synthesis from syngas containing CO2. The correlations of methanol space time yield (STY) versus the physicochemical characteristics of Cu/ZnO catalysts were studied. The catalyst with equal amounts of Cu and Zn displayed the best catalytic activity owing to higher Cu0 surface area, more oxygen vacancy and ZnO(002) plane, as well as more moderately basic sites.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18600?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18600</a>.Reaction equipment; Cu 2p and Zn 2p XPS spectra of the calcined catalysts; correlation between the maximum reduction temperature and Ovacancy/Olattice ratio; Cu 2p and Zn 2p XPS spectra of the reduced catalysts; Cu LMM Auger spectrum of CZ-R-0.5 catalyst; reaction route of high-temperature ICI process for methanol synthesis; new reaction route of methanol synthesis at low temperatures using methanol itself as a catalytic promoter; variation of total carbon conversion of CZ-R-0.5 catalyst with time on stream; XRD patterns of the CZ-R-0.5 sample before and after reaction; and results of comparison with CO2 and without CO2 (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18600/suppl_file/am0c18600_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

The Sintering of a Cu-Based Methanol Synthesis Catalyst

Microstructure Characters of Cu/ZnO Catalyst Precipitated Inside Microchannel Reactor

Dynamic Transformation of Active Components in Cu-ZnO-Al_2O_3 Catalyst for Methanol Synthesis at High Temperature

Influence of the Calcination on the Activity and Stability of the Cu/ZnO/Al2O3 Catalyst in Liquid Phase Methanol Synthesis

Effects of Pore Structure on Methanol Selectivity in Carbon Monoxide Hydrogenation

Reversible and Irreversible Structural Changes in Cu/ZnO/ZrO 2 Catalysts during Methanol Synthesis

Structure-Performance Correlations over Cu/ZnO Interface for Low-Temperature Methanol Synthesis from Syngas Containing CO2.

Structure–Performance Correlations over Cu/ZnO Interface for Low-Temperature Methanol Synthesis from Syngas Containing CO 2

Doubling the life of Cu/ZnO methanol synthesis catalysts via use of Si as a structural promoter to inhibit sintering

Ultra-high thermal stability of sputtering reconstructed Cu-based catalysts

Cuo/Zno/Al2o3 Catalyst Prepared by Mechanical-Force-Driven Solid-State Ion Exchange and Its Excellent Catalytic Activity under Internal Cooling Condition

Preparation of Cu-based Catalysts for Methanol Synthesis in a Fluidized Bed Reactor and Their Performance

Optimizing Methanol Synthesis from CO2 Hydrogenation over Inverse Zr-Cu Catalyst

Enhanced sintering resistance of bimetal/SBA-15 catalysts with promising activity under a low temperature for CO methanation

Complete Liquid Phase Preparation and Characterization of CuZnAlSi Catalysts for DME Synthesis in Slurry Reactor

CO2 Hydrogenation to Methanol over Partially Embedded Cu Within Zn-Al Oxide and the Effect of Indium

Copper crystallite size and methanol synthesis catalytic property of Cu-based catalysts promoted by Al, Zr and Mn

CO2 Hydrogenation to Methanol over Cu/ZnO/ZrO2 Catalysts Prepared Via a Route of Solid-State Reaction

Surface Properties of CuO/ZnO/Al_2O_3 Catalyst for Methanol Synthesis in Slurry Reactor

Methanol Synthesis from CO2 Hydrogenation with a Cu/Zn/Al/Zr Fibrous Catalyst

Structural Evolution and Catalytic Properties of Nanostructured Cu/Zro2 Catalysts Prepared by Oxalate Gel-Coprecipitation Technique