Abstract:A precursor CuO/ZnO/Al2O3 catalyst for methanol synthesis has been prepared at room temperature by introducing a ternary salt solution into the excess of sodium carbonate solution following the reverse co-precipitation method. The catalyst was tested for the synthesis of methanol from synthesis gas. The composition (vol. %) has been presented: CO, 22; CO2, 5.8; N2, 5.5; H2, balance. The methanol productivity was recorded to be 2.7 kg kgcat–1 h–1 at a temperature of 260 °С, a pressure of 3 MPa, and a space velocity of 61,700 l (kgcat)–1 h–1. The possibility of regenerating the activity of a catalyst subjected to conditions of artificial aging (overheating in a syngas environment) has been tested: approximately 92% of the initial activity could be restored. Physicochemical studies were conducted using the thermogravimetric analysis (TGA), Fourier-transform infrared spectroscopy (FTIR), the scanning electron microscopy (SEM), and the X-ray diffraction (XRD) techniques using the Cu, Zn, and Al oxides obtained following the co-precipitation method. X-ray studies revealed that an amorphous phase was obtained from the Al oxide that was synthesized following both the direct and reverse co-precipitation methods. The calcination temperature was 300 °C. Individual oxides of Cu and Zn obtained following the reverse co-precipitation method form crystalline phases when calcined at 300 °C. When all three ingredients are present, calcination of the sample at 300 °C helps obtain an X-ray amorphous structure of the catalyst characterized by a high specific surface area. High-temperature carbonates are formed from samples prepared using a ternary mixture of nitrate salts when these are calcined at 300 °C.

Cuo/Zno/Al2o3 Catalyst Prepared by Mechanical-Force-Driven Solid-State Ion Exchange and Its Excellent Catalytic Activity under Internal Cooling Condition

CO2 Hydrogenation to Methanol over Cu/ZnO Catalysts Synthesized Via a Facile Solid-Phase Grinding Process Using Oxalic Acid

Strong Cu/ZnO Interfacial Interaction Induced by ZrO2 Promoter Suppressing the Ethanol Formation in Industrial Methanol Synthesis

A High Activity Cu/ZnO/Al2O3 Catalyst for Methanol Synthesis: Preparation and Catalytic Properties

Preparing methods of CuO/ZnO/Al2O3 catalysts for the synthesis of methanol

CO2 Hydrogenation to Methanol over Cu/ZnO/ZrO2 Catalysts Prepared Via a Route of Solid-State Reaction

Alcohol Solvent Assisted Synthesis of Metallic and Metal Oxide Catalysts: As-Prepared Cu/ZnO/Al 2 O 3 Catalysts for Low-Temperature Methanol Synthesis with an Ultrahigh Yield

Optimization and understanding of ZnO nanoarray supported Cu-ZnO-Al2O3 catalyst for enhanced CO2 -methanol conversion at low temperature and pressure

Preparation of CuO/ZnO/Al2O3 Catalysts for Methanol Synthesis Using Parallel-Slurry-mixing Method

Effective Cu/ZnO/Al2O3 Catalyst for Methanol Production: Synthesis, Activation, Catalytic Performance, and Regeneration

Cu/ZnO/Al2O3 Catalyst Modulated by Zirconia with Enhanced Performance in CO2 Hydrogenation to Methanol

Modulation of Al2O3 and ZrO2 composite in Cu/ZnO-based catalysts with enhanced performance for CO2 hydrogenation to methanol

A practical approach for the preparation of high activity Cu/ZnO/ZrO2 catalyst for methanol synthesis from CO2 hydrogenation

High-Performance Cu/ZnO/Al 2 O 3 Catalysts for CO 2 Hydrogenation to Methanol

A highly efficient Cu/ZnOx/ZrO2 catalyst for selective CO2 hydrogenation to methanol

Dynamic Transformation of Active Components in Cu-ZnO-Al_2O_3 Catalyst for Methanol Synthesis at High Temperature

A Modified Two-Step Coprecipitation Method Provides Better CuZnO/Al2O3 Methanol Synthesis Catalyst with More Uniform Distribution of Alumina

Comparative Surface Studies of High-Zn-level and Commercial Cu/ZnO/Al<sub>2</sub>O<sub>3</sub>Catalysts

High-performance Al-doped Cu/ZnO catalysts for CO 2 hydrogenation to methanol: MIL-53(Al) source-enabled oxygen vacancy engineering and related promoting mechanisms

Dissecting ZnO X /Cu interfacial self-encapsulation and methanol-induced strong metal-support interaction of the highly active alloyed CuZn and ZnO for methanol steam reforming

Synthesis, characterization and activity pattern of Cu–ZnO/ZrO2 catalysts in the hydrogenation of carbon dioxide to methanol