Abstract:In this paper, studies are presented on proton exchanged (PE) and annealed proton exchanged (APE) waveguides in Y-cut magnesium doped lithium niobate based on our systematic fabrication and characterizations. The analysis is focused on the optical and structural properties from the measurements of prism coupler, X-ray diffraction and infrared absorption. The evolution of the index profile with annealing is studied. Unlike the Gaussian index profile for the APE waveguides in pure LiNbO3, the index profile of APE waveguides in MgO:LiNbO3 still keeps the characteristics of step-like profile though with a long index tail. From the measurement results of X-ray diffraction, the strain induced by proton exchange depends on the exchange condition in Y-cut MgO:LiNbO3. The lattice distortion in the guiding layer of an as-exchanged waveguide in Y-cut MgO:LiNbO3 can be up to +0.73%, which can be restored to +0.20% by annealing for a short time. The proton exchange causes more serious non-uniformity of the strain in Y-cut MgO:LiNbO3 than that in pure LiNbO3 in our study. It was also found that HNbO3 phase of high hydrogen concentration can be formed more easily in Y-cut MgO:LiNbO3 by proton exchange from the analysis of 3300cm−1 peak in the IR spectra. The intensity of the infrared absorption peak at 3500cm−1 decreases and the broad peak at 3300cm−1 disappears after annealing in Y-cut MgO:LiNbO3 waveguides.

Proton-Implanted Optical Channel Waveguides in Nd 3+>:Mgo:linbo (3): Fabrication, Guiding Properties, and Luminescence Investigation

Low-Dose Ion Implanted Active Waveguides in Nd3+ Doped Near-Stoichiometric Lithium Niobate: Promising Candidates for Near Infrared Integrated Laser

Planar waveguides in neodymium-doped calcium niobium gallium garnet crystals produced by proton implantation

MgO:LiNbO3 Planar Waveguide Formed by MeV O2+ Implantation and Its Annealing Characteristics

Optical Damage of Zr:LiNbO3 Waveguides Produced by Proton Implantation

Low-Loss Channel Optical Waveguide Fabrication in Nd3+-Doped Silicate Glasses by Femtosecond Laser Direct Writing

Helium-Implanted Optical Planar Waveguides in Nd <sup>3+</sup> -Doped Phosphate Glass

Lithium–Niobate Channel Waveguide for the Realization of Long-Period Gratings

Helium-implanted optical planar waveguides in Nd3+-doped phosphate glass

High-performance femtosecond-laser microfabricated lattice-like-cladding waveguides in Er 3+ and MgO co-doped LiNbO 3 crystals for multi-wavelength guidance and luminescence

Preparation and characteristics of the O3+-ion-implanted and femtosecond laser-ablated waveguide in the high-gain Nd3+-doped laser glass

Formation of Color Centers of Optical Waveguide in LN Crystal by Implanting It with 3 MeV Oxygen Ions

Formation of Optical Waveguide and Annealing Behaviour of LiNbO 3 Implanted by 3.0-Mev Nickel Ions

Annealing Effect on Planar Waveguides in LiNbO3 Produced by Oxygen Ion Implantation

Femtosecond laser-inscribed waveguides in Nd3+:Y3+:SrF2 crystals

Mid-infrared Ridge Waveguide in MgO:LiNbO3 Crystal Produced by Combination of Swift O5+ Ion Irradiation and Precise Diamond Blade Dicing

Optimum Exposure Intervals for Light-Induced Optical Waveguides in Lithium Niobate Crystals by Laser Micromachining

Comparative Studies on Annealed Proton Exchange Waveguides in Y-Cut Mgo : Linbo3 and Z-Cut Linbo3

An infrared 2D Nd3+-doped phosphate glass waveguide formed by proton implantation and femtosecond laser ablation

Characterization of Annealed, Proton Exchange Optical Waveguides in Y-cut MgO:LiNbO 3 Crystal

Optical and structural characterization of annealed proton exchange waveguides in Y-cut MgO:LiNbO3