Abstract:The intrinsic stacking fault energy (SFE) of copper under volumetric, longitudinal, and shear strains is investigated using density functional theory (GGA-PBE). Calculations are performed using a copper slab model aligned perpendicular to the (111) intrinsic stacking fault plane. The calculated SFE for unstrained copper is γ = 41 mJ/m2. Results show a strong dependence of γ on strain and distinct behavior for different types of strain: (a) volumetric and longitudinal in the direction perpendicular to the stacking fault, (b) longitudinal parallel to the stacking fault, and (c) shear parallel to the stacking fault. In the first case (a), the SFE decreases monotonically with strain with a slope dγ/dε|ɛ=0 = −0.44 J/m2 and −0.87 J/m2 for volumetric and longitudinal, respectively, and with d2γ/dε2 > 0. In contrast, for longitudinal strain parallel to the stacking fault (b), the SFE dependence exhibits d2γ/dε2 < 0 with a maximum at ε ≈ −0.015. For the case of shear parallel to the stacking fault (c), the SFE is nearly constant at small and moderately large strain, but drops rapidly at very large strain (by a factor of 1/3 for 〈1¯10〉{111} shear at ε = ±0.1). For large 〈112¯〉{111} shear strains, the SFE can either increase or decrease at large strain depending on the sign of the strain. In volumetric or longitudinal (perpendicular to the stacking fault) tension and longitudinal strain in the boundary plane (and for some shear directions), the SFE can become negative, implying a limit on the stability of the fcc crystal structure. The strong dependence of the SFE on strain suggests deep implications for the mechanical properties, microstructural evolution, and dynamic plasticity of metals at high pressure, during severe plastic deformation, and in shock-loading conditions.

Evolution of Stacking-Fault-Tetrahedron-Like Structures in Copper Crystal

Local Lattice Distortion Mediated Formation of Stacking Faults in Mg Alloys

Collapse of stacking fault tetrahedron and dislocation evolution in copper under shock compression

Shearing Mechanisms of Stacking Fault and Anti-Phase-boundary Forming Dislocation Pairs in the Γ′ Phase in Ni-based Single Crystal Superalloy

Stability of stacking fault tetrahedron in twin boundary bicrystal copper under shear

Molecular-dynamics simulations of stacking-fault-induced dislocation annihilation in pre-strained ultrathin single-crystalline copper films

Direct formation of novel Frank loop and stacking-fault tetrahedron complex

Stress-induced formation mechanism of stacking fault tetrahedra in nano-cutting of single crystal copper

Dislocation reaction-based formation mechanism of stacking fault tetrahedra in FCC high-entropy alloy

Determination of Stacking Fault Probability in Fcc Fe-Mn-Si-Al Alloy by Electron Diffraction

Comparison among the Growth Mechanisms of Stacking-Fault, Twin Lamella and Screw Dislocation - A Monte-Carlo Simulation

Melting of Defective Cu with Stacking Faults

Size-dependent Stability of Stacking Fault Tetrahedron in Coherent Twin Boundary Bicrystal: Comparisons among Al, Ni, Cu and Ag

Automated identification of stacking faults and twin boundaries in face-centered cubic crystal

Conversion of stacking fault tetrahedra to bubbles in dual (Kr, He)-beam irradiated copper

Effect of strain on the stacking fault energy of copper: A first-principles study

Shear Response of Grain Boundary Bicrystals with a Stacking Fault Tetrahedron

Compact A15 Frank-Kasper nano-phases at the origin of dislocation loops in face-centred cubic metals

Reconciling experimental and theoretical stacking fault energies in<i> face</i><i>-centered</i><i> cubic</i> materials with the experimental twinning stress

Evolution of Microstructure and its Parameters after Deformation of Polycrystalline Cu-Al Alloys with Different Stacking Fault Energy

Mechanism Transition of Cross Slip with Stress and Temperature in Face-Centered Cubic Metals