Influence of Heat Treatment on Corrosion Behavior of ZCuSn3Zn8Pb6Ni1FeCo Alloy in 3.5% NaCl Solution

王强松,王自东,范明,朱军军,张鸿
2009-01-01
Abstract:ZCuSn3Zn8Pb6Ni1FeCo alloy was prepared by centrifugal process. The specimens experienced water quenching after holding at 850-900 ℃ for 1-3 h and then were aged at 450, 500, 550 and 600 ℃ for 4 h respectively. Using static immersion method, the effect of heat treatment on the corrosion resistance and corrosion behavior of ZCuSn3Zn8Pb6Ni1FeCo alloy in 3.5% NaCl solution was researched by means of XRD, SEM and so on. The results show that the ZCuSn3Zn8Pb6Ni1FeCo alloy is consisted of α-{Cu, Sn} matrix, as well as hard and brittle δ- Cu5.6Sn phase; the precipitates are composed of α-Fe, γ-Fe, CoCu2Sn, Fe3Co7 and Fe4Zn9, while Pb is precipitated as simple substance. Although ZCuSn3Zn8Pb6Ni1 alloy has more excellent corrosion resistance in 3.5% NaCl solution than ZCuSn3Zn8Pb6Ni1FeCo alloy, both have excellent corrosion resistance. The corrosion mechanism is oxygen depolarized reaction, and the corrosion exhibits Fe and Pb lost pit corrosion, and also has features of general corrosion. The corrosion products are divided into three kinds which are Fe-, Pb-related products and copper oxides, respectively. The δ- Cu10Sn3 phase in ZCuSn3Zn8Pb6Ni1 alloy has excellent corrosion resistance.
What problem does this paper attempt to address?