Effect of C additions to the microstructure and wear behaviour of CoCrFeNi high-entropy alloy
Zeling Zhang,Yanfang Ling,Jia Hui,Fei Yang,Xuhai Zhang,Shuyong Tan,Zonghan Xie,Feng Fang
DOI: https://doi.org/10.1016/j.wear.2023.205032
IF: 4.695
2023-06-24
Wear
Abstract:CoCrFeNi high entropy alloys (HEAs) suffer from inferior hardness and low wear resistance. The introduction of hard particles is a common strategy to improve the tribological properties of this kind of alloy. However, the influence of carbide type (M 23 C 6 , M 7 C 3 , and M 3 C 2 ) and its volume fraction on wear resistance is still under debate. In this work, (CoCrFeNi) 100-X C X (x = 0, 1.3, 1.7, 3.5, and 5.4 at. %) HEAs were prepared by vacuum arc melting. M 23 C 6 precipitated in the FCC matrix through a subsequent heat treatment process. The effect of carbon additions on the microstructural evolution and wear behavior of (CoCrFeNi) 100-X C X HEAs was investigated by dry sliding experiments with Al 2 O 3 ceramic balls as counterparts. The results show that the C interstitials increased the lattice constant of the FCC matrix, on the other hand, the size and volume fraction of carbide precipitates increased with the carbon content. The Cr 23 C 6 precipitates appeared at the grain boundaries and interdendritic regions, which is believed to help strengthen the alloy, leading to an increase in its hardness and wear resistance. However, when the C content is greater than 0.28 wt %, the wear rate went up due to the poor toughness and severe three-body abrasive wear.
engineering, mechanical,materials science, multidisciplinary