Abstract:Effects of Al addition (0.0, 0.5, 3.0, 7.2 wt%) on microstructure, texture and mechanical properties of Mg-3.5Ca based alloys were investigated. Our results revealed that the addition of Al to the as-cast Mg-3.5Ca alloy resulted in the transformation of precipitated secondary phase from Mg2Ca to (Mg, Al)(2) Ca, Al2Ca and even Mg17Al12 phase. Moreover, the as-cast microstructure evolution influenced dynamic recrystallization and texture formation in the subsequent extrusion process. As Al content increased from 0.0 to 7.2 wt%, the elongation to fracture (EL) of as-extruded Mg-3.5Ca alloy was monotonously increased from 1.9% to 9.8% in tension, while counterparts were changeless in compression. As-extruded Mg-3.5Ca-3.0Al alloy showed higher yield and ultimate strength increased by about 42.2 MPa and 71.4 MPa than those of extruded Mg-3.5Ca alloy in tension, respectively. Moreover, when Al addition was up to 7.2 wt%, both tensile yield strength and ultimate tensile strength were in steep decline. The effects of Al addition on compressive mechanical properties (compressive yield strength and ultimate compressive strength) were similar to that in tension. Especially, significantly deteriorated tension-compression asymmetry (TCA) of Mg-3.5Ca-7.2Al alloy was ascribed to grain coarsening and secondary phase transformation. Besides, Al addition also had a significant impact on the hardening capacity (Hc) and strain hardening behavior of Mg-3.5Ca alloy. In particular, as 7.2 wt% Al was added, the hardening capacity of the Mg-3.5Ca alloy was significantly increased from 0.09 to 0.56 in tension. As a result, proper Al addition to Mg-3.5Ca alloy could improve the comprehensive mechanical performance, whereas excessive Al addition not only significantly decreased the strength, but also deteriorated the TCA performance.

Behaviour of calcium in Mg-6Li-3Al alloy

Effect of Ca on the Microstructures and Mechanical Properties of Mg-5Li-3AI-2Zn Alloys

Microstructure and mechanical properties of Mg–8Li–xAl–0.5Ca alloys

Effects of Calcium on the Microstructures and Tensile Properties of Mg–5Li–3Al Alloys

Effect of Ca on Microstructure and Mechanical Properties of Mg-6Al Magnesium Alloy

Effects of Ca on the Microstructures and Mechanical Properties of Mg-Li-Al Alloys

Effect of Ca Addition on Grain Refinement of Mg–9Li–1Al Alloy

Effect of Ca on Microstructure and Mechanical Properties of Mg-3Al Magnesium Alloy

Role of Al Content on the Microstructure, Texture and Mechanical Properties of Mg-3.5Ca Based Alloys

Influence of the Al2Ca Phase on Microstructure and Mechanical Properties of Mg–Al–Ca Alloys

Effect of Ca Content on the Mechanical Properties and Corrosion Behaviors of Extruded Mg–7Li–3Al Alloys

Effect of Ca on Microstructure and Mechanical Properties of Mg-Li-Zn Alloy

Microstructure and Mechanical Properties of the As-Cast and Extruded Mg-( 6-11 ) Li-3 Al-CeCa Alloys

Effects of Ca on Mechanical Properties of Mg-6zn-3al Alloy

Microstructures and Mechanical Properties of Mg–Al–Ca Alloys Affected by Ca/Al Ratio

ANALYSIS ON THE MICROSTRUCTURE OF THE AS-CAST AND EXTRUDED Mg-(6-10)Li-3Al-Ce-Ca ALLOYS

EFFECTS OF Ca ADDITION ON THE MICROSTRUCTURES AND MECHANICAL PROPERTIES OF Mg-5Al-0.4Zn BASED CASTING ALLOY

Effect of Ca Modification on the Elemental Composition, Microstructure and Tensile Properties of Al-7Si-0.3Mg Alloy

Effect of Ca on Microstructure and Properties of Mg-Al-Si Alloys

Effects of CaF2 on the Microstructures and Mechanical Properties of Mg-12%Li-1%Al Alloys

Influence of Al Addition on the Microstructure and Mechanical Properties of Mg-Zn-Sn-Mn-Ca Alloys