Abstract:<p>The double-sided electron beam welding (EBW) technique has a prominent advantage that the maximum thickness of the processable plates increases to about twice as much as for single-sided welding. However, there is no in-depth analysis of fatigue properties of the double-sided electron beam welded thick joints with unequal weld penetrations on both sides, especially in the region where two weld seams overlap each other. This research studied low-cycle fatigue properties of the materials in different zones in the thickness direction of a double-sided electron beam welded joint of TC4 titanium alloys with thickness of 140 mm, in which the weld seam on the upper and lower surfaces are about 95 mm and 55 mm in depth respectively. Moreover, S-N curves of the materials in different zones in the thickness direction were obtained. The results showed that low-cycle fatigue properties of the materials in the overlap region (at about 90 mm from the upper surface) of the two weld seams in the double-sided electron beam welded joint were obviously inferior to those in the other zones. By utilizing a high-resolution scanning electron microscope (SEM), the materials in different zones in the thickness direction of the joint were observed. Based on this, it was found that there were more second-phase precipitates in the overlap of the two weld seams compared with the other zones. The microhardness of the overlap region of the two weld seams was found to be higher than those of base metal (BM) and the other zones of the weld seam. Mechanical properties near the overlap region of the two weld seams in the thickness direction of the joint presented most significant heterogeneity, which was one of the important reasons for the weakening of overall mechanical properties of the joint. The research results are of significance for the design and application of a welded structure of titanium alloys with a large thickness in the fields, such as aviation and ships.</p>

Influences of Gap Size on the Fatigue Strength of Welded Titanium Alloy Overlap Joints

Effects of Tensile/compressive Overloads on Fatigue Crack Growth Behavior of an Extra-Low-interstitial Titanium Alloy

Influences of Size and Position of Defects on the Fatigue Life of Electron Beam Welded-Aluminum Alloy Joints

Maximum Interference Fit Size of Hi-lock Bolted Joints

Microstructure and pore sensitivities in very high cycle fatigue behaviors of titanium alloy welded joints under stress ratios

The Effect of Defect Characteristics on Prediction of Fatigue Life of TC4 Titanium Alloy Welded Joints

Nonuniformity of Fatigue Properties of Two‐Sided Electron Beam Welded Joint of Superthick Titanium Alloy

Study on the J-Integral and Failure Assessment Line of Electron Beam Welded Thick TC4-DT Alloy Joints

Analysis of heterogeneity of fatigue properties of double-sided electron beam welded 140-mm thick TC4 titanium alloy joints

Finite Element Analysis of the Influence of Weld Size on the Combined Connection with Bolts and Welds

Fatigue life evaluation for ring-welded lap joints of stainless steel based on fracture mechanics approach

The Influences of Precrack Orientations in Welded Joint of Ti–6Al–4V on Fatigue Crack Growth

Initiation and propagation mechanism of fatigue crack in ultra-thick titanium alloy vacuum electron beam welding joint

Fatigue inhomogeneity of 140 mm thick TC4 titanium alloy double-sided electron beam welded joints

The Influence of Prior Austenite Grain Size on Fatigue Crack Growth Threshold of Welds in Cr-Mo-V Steel Components

Numerical Study on the Impact of Gap Between Sheets on the Quality of Riveted Single-Strap Butt Joints

Fatigue experiment and assessment of butt-welded joints in steel structures considering misalignment and weld geometry effects

Effect of Loading Methods on the Fatigue Properties of Dissimilar Al/Steel Keyhole-Free FSSW Joints

Fretting Fatigue Damage of Titanium Alloy Clinched Structure

A Study on Fatigue Crack Closure Associated with the Growth of Long Crack in a New Titanium Alloy

Microstructural and interface geometrical influence on the mechanical fatigue property of aluminum/high-strength steel lap joints using resistance element welding for lightweight vehicles: experimental and computational investigation