Abstract:<p>The double-sided electron beam welding (EBW) technique has a prominent advantage that the maximum thickness of the processable plates increases to about twice as much as for single-sided welding. However, there is no in-depth analysis of fatigue properties of the double-sided electron beam welded thick joints with unequal weld penetrations on both sides, especially in the region where two weld seams overlap each other. This research studied low-cycle fatigue properties of the materials in different zones in the thickness direction of a double-sided electron beam welded joint of TC4 titanium alloys with thickness of 140 mm, in which the weld seam on the upper and lower surfaces are about 95 mm and 55 mm in depth respectively. Moreover, S-N curves of the materials in different zones in the thickness direction were obtained. The results showed that low-cycle fatigue properties of the materials in the overlap region (at about 90 mm from the upper surface) of the two weld seams in the double-sided electron beam welded joint were obviously inferior to those in the other zones. By utilizing a high-resolution scanning electron microscope (SEM), the materials in different zones in the thickness direction of the joint were observed. Based on this, it was found that there were more second-phase precipitates in the overlap of the two weld seams compared with the other zones. The microhardness of the overlap region of the two weld seams was found to be higher than those of base metal (BM) and the other zones of the weld seam. Mechanical properties near the overlap region of the two weld seams in the thickness direction of the joint presented most significant heterogeneity, which was one of the important reasons for the weakening of overall mechanical properties of the joint. The research results are of significance for the design and application of a welded structure of titanium alloys with a large thickness in the fields, such as aviation and ships.</p>

Study on the J-Integral and Failure Assessment Line of Electron Beam Welded Thick TC4-DT Alloy Joints

Numerical Analysis of Constraint and Strength Mismatch Effects on Local Fracture Resistance of Bimetallic Joints

Fundamental research on electron beam welding of heavy section titanium alloy structures

Zoning Study on the Fatigue Crack Propagation Behaviors of a Double-Sided Electron Beam Welded Joint of TC4 Titanium Alloy with the Thickness of 140 Mm

Study on fracture mechanics parameters of surface crack in overmatched weldments

The Effect of Defect Characteristics on Prediction of Fatigue Life of TC4 Titanium Alloy Welded Joints

Design of Undermatching T Joints Based on the Thought of Equal Load Carrying Capacity

Nonuniformity of Fatigue Properties of Two‐Sided Electron Beam Welded Joint of Superthick Titanium Alloy

Mechanical and Fatigue Properties of Undermatching Butt Joints of 10crni3mov Steel

Microstructure and performance of dissimilar joint QCr0.8/TC4 welded by uncentered electron beam

Study on KIC of TC4-DT titanium alloy electron beam welding

Fatigue experiment and assessment of butt-welded joints in steel structures considering misalignment and weld geometry effects

An Experimental Investigation of In-Plane Constraint Effect on Local Fracture Resistance of A Dissimilar Metal Welded Joint

Analysis of heterogeneity of fatigue properties of double-sided electron beam welded 140-mm thick TC4 titanium alloy joints

Interfacial layer regulation and its effect on mechanical properties of Ti6Al4V titanium alloy and T2 copper dissimilar joints by cold metal transfer welding

Fatigue Properties of Titanium-Clad Bimetallic Steel Butt-Welded Joints

Performance analysis on welded joints made of TC4/TA17 dissimilar titanium alloys

Acceptance levels of misalignment of welded joints under different quality categories

Effects of Welding Parameters on Weld Shape and Residual Stresses in Electron Beam Welded Ti2AlNb Alloy Joints

Prediction of Residual Stresses Distribution in Strength-Mismatched Butt Joints Using Finite Element Method

A Fracture Mechanics-Based Optimal Fatigue Design Method Of Under-Matched Hsla Steel Butt-Welded Joints With Imperfections