Modification of Precipitated Calcium Carbonate Filler Using Sodium Silicate/zinc Chloride Based Modifiers to Improve Acid-Resistance and Use of the Modified Filler in Papermaking
Jing Shen,Zhanqian Song,Xueren Qian,Wenxia Liu
DOI: https://doi.org/10.15376/biores.4.4.1498-1519
2009-01-01
BioResources
Abstract:In order to improve the acid-resistant property of papermaking grade precipitated calcium carbonate filler and to obtain modified filler in powder form, sodium silicate/zinc chloride based modifiers were used in filler modification, and the use of modified filler in papermaking of deinked pulp derived from recycled newspaper was also preliminarily investigated. Under the preliminarily optimized experimental conditions, when sodium silicate, zinc chloride, sodium hexametaphosphate, and phosphoric acid with dosages of 10 wt%, 3 wt%, 1 wt% and 0.2 wt%, respectively, were used as modifiers, and when the temperature, aging time, and PCC concentration during the filler modification process was 70 oC, 7 h and 9.1 wt%, respectively, the acid-resistant property of filler was significantly improved after modification, as evaluated using alum consumption and pH methods. The use of modified precipitated calcium carbonate filler prepared under the optimized conditions provided considerably more brightness and light scattering improvement in comparison to unmodified filler, and filler modification was found to have only negligible influence on tensile and burst strength of the paper, air permeability of the paper, and retention performance of the filler. Surface analysis of the modified filler using XPS and SEM confirmed the occurring of surface encapsulation and modification of precipitated calcium carbonate filler when the relevant modifiers were used in filler modification. The encapsulating effect of modifiers on filler was thought to be favorable to improvement in acid-resistant property, and optical properties of the filled paper.