Influence of pressing and drying on the microstructure of recycled plant fibers

Jinquan Wan,Yan Wang,Yongwen Ma,Qing Xiao

2009-01-01

Cellulose Chemistry and Technology

Abstract:The influence of pressing and drying oil the microstructure of wheat straw fiber during reuse processes was Studied. The results showed that, at an applied pressure below 4 MPa, the WRV loss rate was of 7.96%, while, at pressures over 4MPa, it was of 25.90%. When pressure increased from I MPa to 5 MPa, cellulose crystallinity increased also, and the fiber cell wall pores closed to a great extent. With increasing pressure front I to 5 times, WRV decreased. However, cellulose crystallinity increased with increasing the number of pressings. Fiber pores were irreversibly and significantly closed after the first pressing while, with an increasing number of pressings, the changes observed in pore size and distribution of fibers were insignificant. When the drying temperature increased from 60 to 120 degrees C, cellulose crystallinity increased to 84.6% and the average pore volume corresponding to the mesopore decreased by 5.42 x 10(-5) cm(3)/g. In addition, WRV decreased, cellulose crystallinity increased and the degree of non-reversible closure was enhanced, when increasing the drying time at 100 degrees C. Electronic microscope photographs evidence no non-restorable collapse deformation and folds oil the fiber cell wall after pressing and drying, which modified the sizes and shapes of the fiber cell wall.