Abstract:The chemical-vapor-deposition (CVD) process is sufficiently well developed to allow the large-scale production of carbon nanotubes (CNTs). Metal nanoparticles (Fe, Co, Ni, etc.) are usually immobilized on a solid support and then decompose the gaseous hydrocarbon feedstocks into fragmented carbon units at elevated temperatures of 700-1100°C. Metal carbides are formed and then these dominate the growth of filamentous carbon as a structural template. The produced CNTs cannot stay firmly with an inert support and so inevitably detach away, especially during liquidphase purification or mechanical treatment. The biggest difficulties when handling the loose powder are filtration in the slurry-phase operations and the large pressure drops in fixed-bed reactors. These problems very much limit the application of CNTs on a large scale. The fabrication of carbon filaments on a structured support (e.g., activated carbon, carbon fibers, porous frameworks, graphite) has also suffered from discontinuities in the structure. The future use of CNTs has also been restricted by the technical requirements and the necessary high energy consumption to operate the intense and complicated CVD process. To avoid any mechanical post-treatment of powder and the risk of explosion during CVD synthesis, we have explored a simple method to produce monolithic CNTs directly as millimeter-scale spheres, featuring an integral continuity in the structure from microscopic to macroscopic scales. The whole process of CNTs growth has been conducted in a flow of ultrapure N2, involving a set of elementary steps in the solid phase being less complex than the widely used CVD process. The growth of CNTs is based on a solid reaction mechanism and well-graphitized nanotubes can be obtained even at a temperature as low as 400C. Direct observation of all growth events is made by using in-situ transmission electron microscopy (TEM), X-ray diffraction (XRD), IR, Raman spectroscopy and thermogravimetric analysis. A commercial styrene-divinylbenzene copolymer resin was used as the carbon precursor. According to Scheme 1, the ion-exchanged resin spheres were calcined at 800C in a flow of N2 or vacuum, after which the average diameter decreases from 0.77 to 0.49 mm, while the bulk density increases from 0.55 to 0.91 g ml. A novel macroscopic structure can be clearly seen, especially after the removal of the Fe nanoparticles and the amorphous carbon species by refluxing the spheres in concentrated HNO3. As seen in Fig. 1a, the twisted nanotubes construct the monolith while keeping a spherical shape. The cross-section views of the hand-broken spheres show no difference in the structure between the bulk and the surface, indicating a homogeneous distribution of the nanotubes in the millimeter-scale spheres (Fig. 1b). The nitrogen adsorption/ desorption isotherm shows a hysteresis loop to identify a typical mesoporous feature. The measured BET surface area and the pore volume are 223.7 m g and 0.42 ml g, respectively. The distribution of the pores ranges between about 2 and 15 nm.

Synthesis of Carbon Nanotube Microspheres by Reverse Microemulsion

One-step Syntheses and Properties of Carbon Microspheres with Amino Groups

Influence of NH 4 + on the preparation of carbonaceous spheres by a hydrothermal process

Microemulsion nanoreactor applied for the synthesis of iron-based catalysts for carbon nanotube formation

A New Method to Fabricate Large Amount of Single-Walled Carbon Nanotubes

Spherical Multi-Walled Carbon-Nanotube Architectures : Formation Mechanism and Catalytic Performance

A Treatment Method to Give Separated Multi-Walled Carbon Nanotubes with High Purity, High Crystallization and a Large Aspect Ratio

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

In Situ Fabrication of Carbon Nanotube/Mesocarbon Microbead Composites from Coal Tar Pitch

Controllable and Large-Scale Synthesis of Carbon Nanofibers, Bamboo-Like Nanotubes, and Chains of Nanospheres over Fe/Sno2 and Their Microwave-Absorption Properties

Synthesis of Helical Carbon Nanotubes, Worm-Like Carbon Nanotubes and Nanocoils at 450 °C and Their Magnetic Properties

Optimize the Properties of Carbon Nanotubes Synthesized using a Microwave Oven

Synthesis of Aligned Carbon Nanotube with Straight-Chained Alkanes by Nebulization Method

Carbon nanotubes and carbon nanobeads synthesis by one-pot chemical vapor deposition method: morphology and crystallinity

Large‐Scale Synthesis, Annealing, Purification, and Magnetic Properties of Crystalline Helical Carbon Nanotubes with Symmetrical Structures

Influence of Acid Treatments of Carbon Nanotube Precursors on Ni/Cnt in the Synthesis of Carbon Nanotubes

Robust Synthesis of Silver Nanocubes in Oil Phase

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Thermal CVD Synthesis of Carbon Nanotubes Filled with Single-Crystalline Cu Nanoneedles at Tips

Synthesis of Copper-Core/Carbon-Sheath Nanocables by a Surfactant-Assisted Hydrothermal Reduction/Carbonization Process

Pre-Treatment And Liquid-Phase Fabrication Of Carbon Nanotube Films