Abstract:The membrane formation mechanism of PVDF/DMAc/H2O/Additive system was studied. The additive was PVP, PEG or LiCl respectively. The phase diagram for polymer solution of PVDF/DMAc/Water/Additive system was measured using cloud-point method. The phase separation phenomena during membrane formation process were recorded using light transmission experiment. The crystallinity of membrane was detected by DSC. The result shown both gelation and liquid-liquid demixing existed during phase-inversion process of casting solution with different additive. Gelation appeared early at lower nonsolvent concentration than liquid-liquid demixing in the range of 30 ∼ 60°C. LiCl as additive lead to a strong action for PVDF solution to form gel than PEG or PVP. This increased the mass transfer resistance in nascent membrane and the liquid-liquid demixing delayed time prolonged along with the sequence of PVP, PEG or LiCl as additive during membrane formation process. The polymer concentration of nascent membrane at the onset of liquid-liquid demixing increased and restricted the development of macrovoids. The strong gelation tendency of polymer solution intensified the solidification of nascent membrane and restricted the macrovoids development further. Thus the macrovoids structure extended to the bottom and stopped with the sponge-like structure when PVP was used as additive. When the additive was PEG or LiCl, the macrovoids developed insufficiently and terminated in the middle of membrane with the sponge-like structure and then passed to nodular structure in bottom. The effective porosity and flux decreased and crystallinity increased along with the sequence of PVP, PEG or LiCl as additive. The hydrophobicity of membrane with LiCl as additive was barely changed, but the water-resisting pressure of membrane with PVP or PEG as additive decreased about 20 kPa.

Preparation and Polymerization of Inverse Microemulsion System of Dimethyl Diallyl Ammonium Chloride-Acrylamide

Stability of Emulsion Copolymerization of Acrylic Monomers Containing Amino and Hydroxyl Groups

Phase separation in aqueous stabilizer-free two-phase polymerization

Study on the inverse emulsion polymerization of PDMDAAC-AM

Emulsion Copolymerization of Butyl Acrylate with Cationic Monomer Using Interfacial Redox Initiator System

Influence of additives on phase separation process of PVDF solution and membrane morphology

Effect of 1,4‐dioxane on Synthesis of Macroporous Poly(n‐isopropylacrylamide) Hydrogels

Stability and Phase Behavior of Acrylamide-Based Emulsions Before and after Polymerization.

Efficient demulsification of cationic polyacrylate for oil-in-water emulsion: Synergistic effect of adsorption bridging and interfacial film breaking

Miniemulsification of butyl acrylate containing nanometer silica particles

Inverse Emulsion Polymerization of Acrylamide Initiated by Uv Radiation

Preparation and Characterization of a High Performance Emulsion Using a Polymeric Emulsifier and AKD

Role of Added Amphiphilic Cationic Polymer in the Stabilization of Inverse Emulsions

Research on the Polymerization Process of Preparing Polydimethyldiallylammonium Chloride(PDMDAAC)

Stabilizer-Free Aqueous Two-Phase Copolymerization of Acrylamide and Cationic Monomer: Role of Electrostatic Interactions in the Phase Separation, Colloid Morphology, and Stability

Influence of Alkyl Chain Length on the Performance of Inverse Emulsion Polyacrylamide Fracturing Fluid Thickeners

Dispersion polymerization of nano-organic cationic polymer PDMDAAC-AM

Preparation and Characterization of Poly (N-Isopropylacrylamide-co-dimethylaminoethyl Methacrylate) Microgel Latexes

Preparation and properties of ambient self-crosslinking acrylic emulsion

Demulsification law of polyether demulsifier for W/O crude oil emulsion containing hydrophobically modified polyacrylamide in water

Stability of Emulsion Polymerization of New Fluorinated Acrylate Emulsion and Its Characterization