Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites
Shanyi Du,Lin Xu,Xinghong Zhang,Ping Hu,Wenbo Han
DOI: https://doi.org/10.1016/j.matchemphys.2009.02.039
IF: 4.778
2009-01-01
Materials Chemistry and Physics
Abstract:ZrB2-based ceramic composites containing 20vol.% SiC whiskers were prepared through hot-pressing. Effect of sintering temperature (1650–1950°C) and holding time (30–60min) on the microstructure and mechanical properties of ZrB2–SiCw composites were investigated. Relative density and grain size increased with increasing temperature, from 93% and 3.0μm for 1650°C to 99.5% and 5.6μm for 1950°C. Similarly, relative density and grain size increased when the holding time prolonged from 30min to 45min, and then showed a little increment with further increase of time. Flexural strength and fracture toughness were improved with hot-pressing temperature increased, except 1950°C. Analysis suggested that mechanical properties were limited by the thermal instability of SiC whiskers at such high temperature. Meanwhile, flexural strength increased as the increase of holding time. However, no obvious increment was found for fracture toughness, which was probably attributed to the residual pores.