Effects of high temperature heat treatment on the microstructure of Nb-Cr based multi-element alloy

Mingjun Zhang,Xiping Guo

DOI: https://doi.org/10.3321/j.issn:1002-185x.2008.05.029

2008-01-01

Rare Metal Materials and Engineering

Abstract:A master alloy ingot of Nb-Cr based multi-element alloy has been prepared by a vacuum non-consumable arc-melting and then a vacuum consumable arc-melting. The samples are then heat treated at 1250 degrees C/24 h, 1350 degrees C/24 h and 1450 degrees C/24 h, respectively. Both the arc-melted microstructure and the heat-treated microstructure are characterized by using X-ray diffractometer, optical microscope (OM) and scanning electron microscope (SEM) equipped with energy dispersive spectrum analyzer (EDS). The results show that the arc-melted microstructure was composed of Nb solid solution (Nbss) dendrites and Laves Cr-2(Nb, Ti, Hf) blocks dispersed in the Nbss dendrite intervals; after heat treatments, the phase constituents of alloy are same as those in the arc-melted microstructure. However, the microstructure is refined, and the Nbss dendrites disappeare and are transformed into equiaxed crystals. Furthermore, the fine and dispersed secondary Cr-2(Nb, Ti, Hf) are precipitated in the Nbss matrix. With the increase of heat treatment temperature, the microstructure became finer, and the amount of Cr-2(Nb, Ti, Hf) increases.