Effect of Fired Temperature on Microstructure and Superconductivity of MOD-YBCO Thin Films

Lianhong Wang,Tao Li,Fazhu Ding,Xudong Lü,Hongwei Gu

DOI: https://doi.org/10.3969/j.issn.0258-7076.2008.04.013

2008-01-01

Abstract:Epitaxial YBCO superconducting thin films were prepared by metal organic deposition(TFA-MOD) method on single crystalline LaAlO3(001) substrate and adopting heat treatment temperature was in the range of 780～860 ℃,and microstructure and superconductivity of YBCO thin films were characterized by means of scanning electron microscope(SEM) and Jc-scan system.X-ray diffraction method(XRD) results showed that with the temperature rising BaF2 in the films decreased and the grains grown in c-axis orientation of texture increased,but that in a-axis orientation and impurity phases decreased as the temperature was within 780～820 ℃;as the temperature was within 820～860 ℃,with the temperature increasing the grains grown in c-axis orientation of texture decreased and that in a-axis increased.From SEM observation of the YBCO films it was found that the surface of the film was smooth and without micro crack.The result of testing superconducting property showed that Jc value of the YBCO film treated at 820 ℃ was 1×106 A·cm-2 at 77 K,in self-field.