Polycondensation of L-aspartic Acid under Microwave Irradiation
许迎春,吴一弦,孔祥璐,杨维曦,徐日炜,杨万泰,武冠英
DOI: https://doi.org/10.3969/j.issn.1671-4628.2009.03.009
2009-01-01
Abstract:The polycondensation of L-aspartic acid (A) was conducted in a mixed solvent of sulpholane and 1,3,5-trimethylbenzene with phosphoric acid (φ=85%) as catalyst, using microwave irradiation. The effects of varying the dosage of phosphoric acid catalyst, microwave power, reaction temperature and time on the yield, average molecular weight and molecular weight distribution (MWD, Mw/Mn) of the resulting polymer products, poly(succinimide) (PSI) and poly(aspartic acid), was investigated. The product polymers, were characterized by FT-IR. The results indicated that, compared with the traditional method, under microwave irradiation the polymerization time could be significantly reduced from 3-5 h to 20 min, and the reaction temperature (170-200 ℃) required was also reduced. The yield and molecular weight increased with increasing reaction temperature and time. All the GPC traces of the poly(aspartic acid) products obtained with different concentrations of catalyst exhibited narrow and unimodal molecular weight distributions with number-average molecular weight (Mn) from 6000 to 20000 and polydispersity from 1.3 to 2.4.