Phase separation and morphology formation of Co-Cu-Si ternary alloy

Jianqi Yuan,FuPing Dai,Ying Ruan,Bingbo Wei
2008-01-01
Xibei Gongye Daxue Xuebao/Journal of Northwestern Polytechnical University
Abstract:The rapid solidification of Co45Cu45Si10 and Co25Cu25Si50 ternary alloys under free fall is achieved. The experimental undercooling of Co45Cu45Si10 and Co25Cu25Si50 alloys is up to 357 K(0.22TL) and 320 K(0.20TL), respectively. The liquidus temperature of Co45Cu45Si10 and Co25Cu25Si50 alloys is determined as 1600 K and 1592 K, and the solidus temperature of Co45Cu45Si10 and Co25Cu25Si50 alloys is determined as 1358 K and 1105 K, respectively. The critical undercooling of liquid phase separation of Co45Cu45Si10 ternary alloy is only 8 K. The L+α-Co→ε-Co peritectic transformation takes place during metal droplets whose diameters are larger than 100 μm, and solidified microstructure is composed of (Cu), ε-Co and α-Co phases. If the diameter of alloy droplet is smaller than 100 μm, the solidified microstructure is mainly composed of (Cu) and ε-Co phases. The critical separation undercooling does not exist in Co25Cu25Si50 ternary alloy melt, and no phase separation microstructure is found in this alloy. The rapid solidification microstructure of Co25Cu25Si50 alloy is composed of CoSi, CoSi2 and Cu3Si three intermetallic compounds. Though nucleation rate of Cu3Si phase is maximal, it never acts as the leading phase. When ΔT>127 K, the primary phase is dendritic of CoSi2 phase. Once ΔT>127 K, the primary phase changes to the dendritic of CoSi phase.
What problem does this paper attempt to address?