Abstract:The dielectric properties, infrared (IR) dielectric response and Raman spectra of tunable microwave (MW) Ba1−xSrxTiO3 (x=0.4, 0.5, 0.6 and 0.7) ceramics were studied systematically as functions of composition and temperature. It was found that, with increasing the content of Sr from 40% to 70%, the permittivity of the Ba1−xSrxTiO3 ceramics decreased from 7200 to 640 while the dielectric tunability decreased from 50.1% to 5.4% measured at 10kHz. It is particularly interesting that the MW dielectric loss tangent was significantly decreased from 1.5×10−2 to 7.4×10−4. Complex permittivity spectra obtained by fitting the infrared data were also extrapolated to MW frequency and compared with the dielectric data near 1GHz. For the samples with x=0.4 and x=0.5, the dielectric loss measured at ∼1GHz was much higher than that calculated at 10GHz, which is presumably due to the Debye-type dielectric relaxation in GHz region. However, the dielectric loss of the samples with x=0.6 and x=0.7, extrapolated from IR range, was in agreement with that measured at MW frequency. Low-temperature Raman scattering showed that the band at 760cm−1 assigned to the Ti−O3 torsional mode markedly sharpens and shifts upward with increasing content of Sr. This is an indication that the bonding between cations and anions was tightened due to the substitution of Ba with Sr, which explains well the decrease in dielectric permittivity, loss and tunability with increasing concentration of Sr.

Effect of Additive SrWO 4 on Microwave Dielectric Properties of SrTiO 3 –sr(mg 1/3 Nb 2/3 )O 3 Ceramics

Effects of (mg1/3nb2/3) Substitution on the Structure and Microwave Dielectric Properties of Sr2TiO4 Ceramics

Microwave Dielectric Properties of Temperature Stable (1-X)srlaalo4-xtio2 Composite Ceramics

Influence of Low Concentration Mgco2(Vo4)(2) Addition on Microwave Dielectric Properties of Ba0.6sr0.4tio3 Ceramics

Effect of MgWO4 Content on Properties of Ba0.5Sr0.5TiO3 Composite Ceramics for Tunable Microwave Applications

Microwave dielectric properties of Li2WO4-added SrWO4 ceramics for LTCC applications

Study on Microwave Dielectric Properties of SrTiO3/Mg6Ti5O16 Composite Ceramics

Structure and Microwave Dielectric Characteristics of Sr-2[Ti1-x(Al0.5Nb0.5)(x)]O-4 (x <= 0.50) Ceramics

Dielectric Tunable Properties of Ba 0.5 Sr 0.5 TiO 3 –mgmoo 4 Composite Ceramics for Microwave Applications

Microwave Dielectric Properties of Novel (1 − X)mgtio3–xca0.5sr0.5tio3 Ceramics

Microstructures and dielectric properties of (1− x )SrTiO 3 – x Ca 0.61 Nd 0.26 TiO 3 ceramic system at microwave frequencies

Crystal structure and dielectric properties of (1− x )SrTiO 3 - x Ca 0.4 Sm 0.4 TiO 3 ceramic system at microwave frequencies

B-site Substitution by (Mg$lt;inf$gt;1/3$lt;/inf$gt;Ta$lt;inf$gt;2/3$lt;/inf$gt;)$lt;sup$gt;4+$lt;/sup$gt; on Structures and Dielectric Properties of New Sr-based (Sr, Nd, Ca)TiO$lt;inf$gt;3$lt;/inf$gt; Microwave Ceramics

Microwave dielectric properties of the high dielectric (1-x)Ca0.7Nd0.2TiO3-xBa0.4Sr0.6TiO3 ceramics

Structure and Microwave Dielectric Characteristics of Solid Solutions in SrNdAlO4‐Sr2TiO4 System

Temperature Stable and Low Loss Microwave Dielectric Ceramics of Li2Mg3-xSrxTiO6

Effects of adding B<sub>2</sub>O<sub>3</sub> on microwave dielectric properties of 0.9625MgTiO<sub>3</sub>-0.0375(Ca<sub>0.5</sub>Sr<sub>0.5</sub>)TiO<sub> 3</sub> composite ceramics

Microwave and Infrared Dielectric Response of Tunable Ba1−xSrxTiO3 Ceramics

Study on the microwave dielectric properties of 0.84MgNb2-x(Ti1/2W1/2)xO6-0.16CaTiO3 ceramic

Structure, Chemical Bond, and Microwave Dielectric Properties of (sr1−xcax)2(ti1−xsnx)o4 Ceramics

Microwave dielectric properties of Ba 2Ca 1-xSr xWO 6double perovskites