Abstract:Understanding the corrosion behavior of Fe-based amorphous coatings under wet-dry cyclic conditions is of pretty importance for coating applications in marine environments. In this paper, the corrosion evolutions of the coatings under wet-dry cyclic conditions were investigated by electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM) and transmission electron microscopy (TEM). Accurate charge transfer resistance (Rt) was obtained through fitting EIS results using a modified transmission line equivalent circuit model and a landscape map of Rt was constructed for a panoramic investigation on coating corrosion. The results show that the corrosion rate of the coating changes cyclically under wet-dry cyclic conditions. Corrosion within a single wet-dry cycle can be presented as four stages: an initial decrease of corrosion rate due to passivation or repassivation when the coating is wetted, then a slow increase due to concentrated aggressive ions with solution evaporation, followed by a rapid increment associated with fast oxygen transport under ultrathin solution film and finally a stable stage as solution dries out. It is deduced that an oxygen concentration gradient can form between the inside and the outside of coating pores when the solution film over the coating is very thin, which further promotes the localized corrosion in the pores. According to the landscape map of Rt, the coating maintains its high corrosion resistance for the initial 33 wet-dry cycles. But its corrosion resistance decreases significantly in the 35th wet-dry cycle accompanied by the attack of localized corrosion. After 65 wet dry cycles, the coating fails due to the penetration of localized corrosion. The interparticle oxide layers are defective, which enhances the localized corrosion process.

MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION III.SPREADING BEHAVIORS OF MICRO-DROPLETS UNDER CYCLIC WET-DRY CONDITIONS

MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION——II.Electrochemical Characteristics of the Micro-Droplets Phenomenon

Wetting Behaviors and Mechanism of Micro Droplets on Hydrophilic Micropillar-Structured Surfaces

Investigation on Micro-Droplet Phenomenon in the Early Atmospheric Corrosion

MICRO- DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION——Ⅰ.Formation and Spreading of Micro- Droplets

Mechanisms of Secondary Spreading and Micro Droplet Formation on Steel

Electrochemical Investigations of Micro-Droplets Formed on Metals During the Deliquescence of Salt Particles in Atmosphere

Visualizing and understanding corrosion evolution beneath a condensed droplet using the multi-electrode array

In Situ Observation of Formation and Spreading of Micro-Droplets on Magnesium and Its Alloy under Cyclic Wet–dry Conditions

The Deliquescence and Spreading of Sea Salt Particles on Carbon Steel and Atmospheric Corrosion

EIS STUDY ON THE DETERIORATION PROCESS OF ORGANIC COATINGS UNDER IMMERSION AND CYCLIC WET-DRY CONDITIONS

Comparative Studies on the Deterioration Process of Organic Coatings under Immersed and Cyclic Wet-Dry Conditions by EIS

Insight into the Corrosion Evolution of Fe-based Amorphous Coatings under Wet-Dry Cyclic Conditions

Sessile multidroplets and salt droplets under high tangential electric fields

Research on the Asymmetric Phenomenon of Voltage Polarity Based on Dielectric Wetting

Anisotropic spreading of droplets on striped electrodes

Micro-Droplets Formation During the Deliquescence of Salt Particles in Atmosphere

Electrochemical Formation Mechanism of Microdroplets on Pure Iron

On-line Monitoring, Data Analysis for Electrolytic Corrosion of ±800 Kv High Voltage Direct Current Insulators

Corrosion Micro- and Macro-Electrochemical Behavior of Rusted Carbon Steel and Weathering Steel

SRB CORROSION OF PETROLEUM TUBULAR MATERIALS