Abstract:<p>Despite historically being the focus of much research and measurement development, atmospheric corrosion under saline droplets and its underlying mechanisms continues to require more accurate investigations. Toward this goal, the electrochemical distributions of pure iron under different volumes of 3.5% NaCl droplets at different elapsed times were investigated using newly developed concentric three-electrode array measurements. The results showed that the electrochemical distribution under a droplet was directly affected by the droplet size. Distributions of corrosion potential and galvanic current on the CTEA under a 110 μL droplet were circumferentially symmetric; whereas, the electrochemical distribution under a 25 μL droplet was characterized by a neighboring peak-valley pair, and that of a 340 μL droplet exhibited multiple adjacent peaks and valleys. The asymmetric electrochemical distributions under droplets with volumes of 25 μL and 340 μL can be attributed to the difference between the droplet sizes and the effective influencing distance of the corrosion couple, which is determined by the corrosion potential difference between the anode and cathode, the galvanic current, and the anodic and cathodic polarizabilities. The standard deviations of galvanic current trend indicated a greater tendency towards localized corrosion under the 110 μL droplet after a coupling period of 60 min. The results suggested that a droplet with the proper size and electrochemical distribution symmetry is more likely to initiate and develop local atmospheric corrosion.</p>

MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION——II.Electrochemical Characteristics of the Micro-Droplets Phenomenon

Investigation on Micro-Droplet Phenomenon in the Early Atmospheric Corrosion

MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION III.SPREADING BEHAVIORS OF MICRO-DROPLETS UNDER CYCLIC WET-DRY CONDITIONS

MICRO- DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION——Ⅰ.Formation and Spreading of Micro- Droplets

Electrochemical Investigations of Micro-Droplets Formed on Metals During the Deliquescence of Salt Particles in Atmosphere

Micro-Droplets Formation During the Deliquescence of Salt Particles in Atmosphere

Visualizing and understanding corrosion evolution beneath a condensed droplet using the multi-electrode array

Electrochemical Formation Mechanism of Microdroplets on Pure Iron

Local electrochemical characteristics of pure iron under a saline droplet I: Effect of droplet size on electrochemical distribution

Mechanisms of Secondary Spreading and Micro Droplet Formation on Steel

The Deliquescence and Spreading of Sea Salt Particles on Carbon Steel and Atmospheric Corrosion

Strategies of metal corrosion protection

Strain-Induced Corrosion Kinetics at Nanoscale Revealed in Liquid: Enabling Control of Corrosion Dynamics of Electrocatalysis

In Situ Observation of Formation and Spreading of Micro-Droplets on Magnesium and Its Alloy under Cyclic Wet–dry Conditions

Microdroplet-Mediated Multiphase Cycling in a Cloud of Water Drives Chemoselective Electrolysis

Sessile multidroplets and salt droplets under high tangential electric fields

REVIEW OF ATMOSPHERIC CORROSION OF ZINC AND ZINC ALLOY

Chemical and Electron Microbial Influenced Corrosion

On-line Monitoring, Data Analysis for Electrolytic Corrosion of ±800 Kv High Voltage Direct Current Insulators

Corrosion of Zinc in Simulated Acid Rain Solution and under Thin Electrolyte Layer Formed by Simulated Acid Rain Solution

The Effect of External DC Electric Field on the Atmospheric Corrosion Behaviour of Zinc under a Thin Electrolyte Layer