Temperature Dependence on Γ/γ' Partitioning Behaviors of Alloying Elements and Γ/γ' Interfacial Energy of a Mo-rich Ni Based Single Crystal Superalloy
Cheng Ai,Jiahui Yang,Yi Ru,Heng Zhang,Shusuo Li,Shengkai Gong,Xinhao Dang,Min Guo,Taiwen Huang,Lin Liu
DOI: https://doi.org/10.1016/j.jallcom.2024.176972
IF: 6.2
2024-01-01
Journal of Alloys and Compounds
Abstract:Based on three-dimensional atom probe technique and Ardell method, the influences of temperature (850degree celsius similar to 1150degree celsius) on microstructure, compositions and solid solution strengths of gamma and gamma ' phases, gamma/gamma' partitioning behaviors of alloying elements and gamma/gamma' interfacial energy of a Mo-rich Ni based single crystal superalloy were investigated. After quenching from 1100degree celsius, microstructure was basically similar as heat-treated state. However, after quenching from 1150degree celsius, gamma ' phase obviously re-dissolved, and gamma channel obviously widened. Meanwhile, with increasing temperature, Co, Cr, Mo and Re contents in gamma phase decreased, while Al and Ta contents in gamma phase increased. With increasing temperature, Co, Cr and Re contents in gamma ' phase slightly decreased, Mo content in gamma ' phase significantly decreased, while Al and Ta contents in gamma ' phase increased. Meanwhile, with increasing temperature, solid solution strength of gamma phase decreased, while solid solution strength of gamma ' phase increased. In addition, with increasing temperature, partitioning ratios of Co, Cr and Re elements decreased, partitioning ratios of Mo and Al elements increased, while partitioning ratio of Ta firstly decreased and then increased. Moreover, both gamma/gamma ' interfacial width and gamma/gamma ' interfacial energy decreased with increasing temperature.