DTA research of a third generation Ni-based single crystal superalloy

Sha Jiao,Jun Zhang,Tao Jin,Changshuai Wang,Haifeng Wang,Lin Liu,Hengzhi Fu
DOI: https://doi.org/10.3969/j.issn.1002-185x.2013.05.031
2013-01-01
Rare Metal Materials and Engineering
Abstract:The effect of the melt overheating temperature on solidification characteristics and microstructure of a third generation Ni-based single crystal superalloy was studied by the Differencial Thermal Analysis (DTA) and the melt superheating treatment. The results show that as the melt overheating temperature increases from 1450 to 1500 degrees C, the nucleation supercooling and solidification interval change a little, the nucleation and growth of 7 phase are in a wide range of temperature. When the melt overheating temperature is above 1580 degrees C, the nucleation supercooling increases sharply and the solidification interval decreases obviously. At the same time, the temperature range of nucleation and growth of gamma phase is reduced, the precipitation of gamma/gamma' eutectic is decreased, and the precipitation temperature of gamma' phase is elevated by 9 degrees C compared with the one overheated to 1450 degrees C. When the melt overheating temperature rises to 1650 degrees C, the nucleation supercooling decreases, and the solidification interval increases appreciably. As the melt superheating temperature. increases from 1500 to 1580 degrees C, the dendrite structure is refined significantly, but then coarsened slightly when the melt superheating temperature rises to 1650 degrees C. The results are primarily attributed to the melt structure change caused by the melt overheating temperature, and the solidification characteristics and microstructure of alloy are affected finally.
What problem does this paper attempt to address?