Abstract:Bleached bamboo pulp, as a kind of natural cellulose, has received significant attention in the field of biomass materials due to its advantages of environmental protection and the abundance of raw materials. Low-temperature alkali/urea aqueous system is a green dissolution technology for cellulose, which has promising application prospects in the field of regenerated cellulose materials. However, bleached bamboo pulp, with high viscosity average molecular weight (Mη) and high crystallinity, is difficult to dissolve in an alkaline urea solvent system, restraining its practical application in the textile field. Herein, based on commercial bleached bamboo pulp with high Mη, a series of dissolvable bamboo pulps with suitable Mη was prepared using a method of adjusting the ratio of sodium hydroxide and hydrogen peroxide in the pulping process. Due to the hydroxyl radicals being able to react with hydroxyls of cellulose, molecular chains are cut down. Moreover, several regenerated cellulose hydrogels and films were fabricated in an ethanol coagulation bath or a citric acid coagulation bath, and the relationship between the properties of the regenerated materials and the Mη of the bamboo cellulose was systematically studied. The results showed that hydrogel/film had good mechanical properties, as the Mη is 8.3 × 104 and the tensile strength of a regenerated film and the film have values up to 101 MPa and 3.19 MPa, respectively. In this contribution, a simple method of a one-step oxidation of hydroxyl radicals to prepare bamboo cellulose with diversified Mη is presented, providing an avenue for a preparation of dissolving pulp with different Mη in an alkali/urea dissolution system and expanding the practical applications of bamboo pulp in biomass-based materials, textiles, and biomedical materials.

Mechanism of Co-salen Biomimetic Catalysis Bleaching of Bamboo Pulp

Cellulose Nanowhiskers from Moso Bamboo Residues: Extraction and Characterization

ZnCl2 Pretreatment of Bamboo Chips to Produce Chemi-Thermomechanical Pulp: Saving Refining Energy and Improving Pulp Properties

The Effects of NaOH-Urea Aqueous Solution on the Strength and Softness Properties of Bamboo Ligno-cellulosic Fibers

Mechanical and thermal properties of sodium silicate treated moso bamboo particles reinforced PVC composites

Reaction mechanism of Co-salen complex catalyzed oxidation of dimeric lignin model compound

Effect of deep eutectic solvent pretreatment on the structure and physicochemical properties of lignin from bamboo shoot shell

Physicochemical Properties of Lignin from Bamboo (Dendrocalamus latiforus) Shoot Shell

Composition and Structure of an Antioxidant Acetic Acid Lignin Isolated from Shoot Shell of Bamboo (dendrocalamus Latiforus)

Effects of Rhamnolipids on Enzymatic Hydrolysis of Bamboo Biomass and Mechanism

Characterization of extracted lignin of bamboo (Neosinocalamus affinis) pretreated with sodium hydroxide/urea solution at low temperature

Effect of Pretreatments on the Enzymatic Hydrolysis of High-Yield Bamboo Chemo-Mechanical Pulp by Changing the Surface Lignin Content

Bamboo fibre processing: insights into hemicellulase and cellulase substrate accessibility

Structural Evolution of Cellulose from Bamboo Fibers and Parenchyma Cells during Ionic Liquid Pretreatment for Enhanced Hydrolysis

CAOSA-extracted lignin improves enzymatic hydrolysis of cellulose

Effect of alkali treatment on enzymatic hydrolysis of p-toluenesulfonic acid pretreated bamboo substrates

One-Step Treatment for Upgrading Bleached Bamboo Pulp to Dissolving Pulp High Solvency in Green Alkali/Urea Aqueous Solution

Integrating Benzenesulfonic Acid Pretreatment and Bio-Based Lignin-Shielding Agent for Robust Enzymatic Conversion of Cellulose in Bamboo

Structural elucidation of lignin, hemicelluloses and LCC from both bamboo fibers and parenchyma cells

Efficient separation of cellulose from bamboo by organic alkali

Enhancing Enzyme-Mediated Cellulose Hydrolysis by Incorporating Acid Groups Onto the Lignin During Biomass Pretreatment