Abstract:In the present study, cellulose was effectively separated from eucalyptus wood with ternary solvents containing organic base 1,1,3,3-tetramethyl guanidine and other organic solvents such as morpholine, N-ethyl morpholine, dimethyl formamide, glycerin, ethylene glycol and diethylene glycol. It was found that the combination of 1,1,3,3-tetramethyl guanidine with morpholine was favorable for achieving high delignification and less loss of cellulose. The removal of lignin and hemicellulose achieved 89.8% and 81.4% after heating for 6 h at 160 °C, respectively. It was found that the combination of 1,1,3,3-tetramethyl guanidine with morpholine was favorable for achieving high delignification and less loss of cellulose. The removal of lignin and hemicellulose achieved 89.8% and 81.4% after heating for 6 h at 160 °C, respectively. The addition of morpholine and water promoted the dissolution of lignin and reduced the degradation of cellulose. Subsequently, the crude cellulose was further purified through a simplified bleaching process, the final removal of lignin and hemicellulose increased to 98.7% and 97.5% respectively, and cellulose with a purity of 96.9% was achieved. The scanning electron microscopy analysis indicated that the diameter of cellulose bundles decreased from about 250 μm to about 20 μm after organic solvents treatment. The fiber bundle was completely separated into a single fiber with a diameter of about 5–10 μm after bleaching process. X-ray diffraction analysis revealed an increase in the crystallinity of fiber from 69.4% to 83.3%, implying a reduction of lignin and hemicellulose in eucalyptus. Fourier transform infrared spectra revealed the high selective removal of lignin and hemicellulose. Two-dimensional 1 H- 13 C Heteronuclear singular quantum correlation was performed to investigated the structure units and linkages of lignin and found that only the structural signal of C 5 -H 5 in guaiacyl (G 5 ) alone existed in the aromatic region, while the signals -OCH 3 , C γ –H γ in β-O-4' (A γ ) and β-β' (C γ ) remained in the side chain region, indicating that lignin could be effectively degraded and dissolved by the ternary solvents. In conclusion, high purity cellulose was obtained from eucalyptus wood by environmentally friendly and recyclable processes.

Efficient separation of cellulose from bamboo by organic alkali

Cellulose Nanowhiskers from Moso Bamboo Residues: Extraction and Characterization

Ball Milling for Biomass Fractionation and Pretreatment with Aqueous Hydroxide Solutions

Promoting the Disassemble and Enzymatic Saccharification of Bamboo Shoot Shells Via Efficient Hydrated Alkaline Deep Eutectic Solvent Pretreatment

Two-step continuous alkali pretreatment for fractionation of the carbohydrates from bamboo and cotton stalk

Composition and Structure of an Antioxidant Acetic Acid Lignin Isolated from Shoot Shell of Bamboo (dendrocalamus Latiforus)

Structural Characteristics and Antioxidant Activities of Acetic Acid Lignin from Bamboo Shell

Green, efficient extraction of bamboo hemicellulose using freeze-thaw assisted alkali treatment

Effects of Rhamnolipids on Enzymatic Hydrolysis of Bamboo Biomass and Mechanism

Isolation, Chemical Characterization, and Immunomodulatory Activity of Naturally Acetylated Hemicelluloses from Bamboo Shavings

Effect of alkali treatment on enzymatic hydrolysis of p-toluenesulfonic acid pretreated bamboo substrates

Integrating Benzenesulfonic Acid Pretreatment and Bio-Based Lignin-Shielding Agent for Robust Enzymatic Conversion of Cellulose in Bamboo

Fractional separation of cellulose from eucalyptus wood through ternary solvents and simplified bleaching treatment

Structural Evolution of Cellulose from Bamboo Fibers and Parenchyma Cells during Ionic Liquid Pretreatment for Enhanced Hydrolysis

Efficient fractionation of bamboo residue by autohydrolysis and deep eutectic solvents pretreatment

Bamboo fibre processing: insights into hemicellulase and cellulase substrate accessibility

Revealing spatial distribution and accessibility of cell wall polymers in bamboo through chemical imaging and mild chemical treatments

Towards the Development of a Novel “Bamboo-Refinery” Concept: Selective Bamboo Fractionation by Means of a Microwave-Assisted, Acid-Catalysed, Organosolv Process

Evaluation of chemical treatments to tensile properties of cellulosic bamboo fibers

One-Step Treatment for Upgrading Bleached Bamboo Pulp to Dissolving Pulp High Solvency in Green Alkali/Urea Aqueous Solution

Revisiting Alkaline Pretreatment of Lignocellulose: Understanding the Structural Evolution of Three Components