Abstract:Thermal barrier coatings (TBCs) are deposited on metallic components to prevent heat flux due to their excellent thermal insulation function. Nowadays, TBCs have become the key core technology of the new generation gas turbines. TBCs prepared by plasma spraying method are more readily to be failed, which negatively affect the thermal insulation and may cause substrate erosion. Therefore, long life span is an important guarantee for TBCs to achieve thermal barrier function. This paper described the failure mechanism of plasma sprayed TBCs and crack-resistant designs. To begin with, the essential characteristics of plasma sprayed TBCs were revealed. Plasma sprayed TBCs appeared to be lamellar structure with connected 2D pores. As a result, the plasma sprayed TBCs have excellent thermal insulation and strain tolerance at as-deposited state. By thermal exposure, the density of 2D pores is decreased significantly, which dominantly account for the degradation of strain tolerance and thermal insulation. Subsequently, the failure mechanism of plasma sprayed TBCs is revealed. The degradation of strain tolerance leads to increase of driving force for cracking. Consequently, the micro-scale cracks are extended and connected to form large-scale cracks, which is responsible for the failure of plasma sprayed TBCs. Finally, cracking-resistant designs are reviewed from two aspects: decreasing driving force and increasing fracture toughness. It is worth noting that the current cracking-resistant design often has poor performance on thermal insulation. In future research, how to ensure high thermal insulation and long life of the coating while considering the economy is the key direction of the development of a new generation of high-performance thermal barrier coatings.

Study of failure mode and failure mechanisms on thermal fatigue of plasma sprayed thermal barrier coatings

Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings

Atmospheric plasma sprayed thick thermal barrier coatings: Microstructure, thermal shock behaviors and failure mechanism

Assessment of Stress Characteristic and Interfacial Delamination in Thermal Barrier Coatings Considering the Connected Crack Network

An Innovative Model Coupling TGO Growth and Crack Propagation for the Failure Assessment of Lamellar Structured Thermal Barrier Coatings

Influence of “Island-Like” Oxides in the Bond-Coat on the Stress and Failure Patterns of the Thermal-Barrier Coatings Fabricated by Atmospheric Plasma Spraying During Long-Term High Temperature Oxidation

Analysis On Stress Distribution Of Thermal Barrier Coating System With Thermal Gradient Mechanical Fatigue

The Combined Effect of Creep and TGO Growth on the Cracking Driving Force in a Plasma-Sprayed Thermal Barrier System

Comprehensive Understanding of Horizontal and Vertical Crack Effects on Failure Mechanism of Lamellar Structured Thermal Barrier Coatings

Dynamic Crack Growth Mechanism and Lifetime Assessment in Plasma Sprayed Thermal Barrier System Upon Temperature Cycling

A Mechanistic Study of Oxidation-Induced Degradation in A Plasma-Sprayed Thermal Barrier Coating System. Part I: Model Formulation

Stress States and Crack Behavior in Plasma Sprayed TBCs Based on a Novel Lamellar Structure Model with Real Interface Morphology

Influences of the Near-Spherical 3D Pore on Failure Mechanism of Atmospheric Plasma Spraying TBCs Using a Macro-Micro Integrated Model

Failure Mechanism and Cracking-Resistant Design of Thermal Barrier Coatings with Long Life Span

Relationship Between Lamellar Structure and Elastic Modulus of Thermally Sprayed Thermal Barrier Coatings with Intra-splat Cracks

Failure Characteristics and Life Prediction for Thermally Cycled Thermal Barrier Coatings

Comprehensive Dynamic Failure Mechanism of Thermal Barrier Coatings Based on a Novel Crack Propagation and TGO Growth Coupling Model

Thermal Fatigue of Atmospheric Plasma Sprayed Thermal Barrier Coatings

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Comprehensive Effects of TGO Growth on the Stress Characteristic and Delamination Mechanism in Lamellar Structured Thermal Barrier Coatings

Numerical Analyses of the Residual Stress and Top Coat Cracking Behavior in Thermal Barrier Coatings under Cyclic Thermal Loading