Abstract:Amorphous Fe73.5-xCoxSi13.5B9Cu1Nb3（x=10,30,50） ribbons were prepared by the single copper wheel melt spinning technique in the air atmosphere.The nanocrystallization kinetics of amorphous ribbons was investigated by differential scanning calorimetry（DSC）.The apparent activation energies of amorphous ribbons were calculated by using Kissinger and Ozawa methods.It was found that the activation energies of the first crystallization reduce and those of the second crystallization rise with increasing Co content.The local Avrami parameter m for primary crystallization was calculated using Johnson-Mehl-Avrami（JMA） model.The values of the Avrami parameter showed that the primary crystallization mechanism of amorphous ribbons varied at different stages.In the initial stage,the crystallization mechanism was bulk crystallization with three dimensional nucleation and grain growth controlled by diffusion.In the following stage,it was surface crystallization with one dimensional nucleation and grain growth at a near zero nucleation rate.The variation of soft magnetic properties of nanocrystalline Fe63.5Co10Si13.5B9Cu1Nb3 powder cores as a function of milling time has been investigated.It was found that the effective permeability of the cores shows high frequency stability and decreases with increasing milling time.The quality factor increases with increasing frequency in the lower frequency range,reaches a maximum at the frequency of 80 kHz,and then decreases gradually with increasing frequency.

Liquid Phase Preparations and Performances of Magnetic Dendritic Nanocrystalline Co

Studies on the magnetic polymer with nanometer magnetic dispersing phase. (3). Studies on preparation and properties of Crx Fe3-xO4 nanocrystalline magnetic carrier

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Growth of Dendritic Cobalt Nanocrystals at Room Temperature

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Manipulation of Morphology and Magnetic Properties in Cobalt Nanowires

Thermo-Decomposition Process of Preparation of Nanometer Cobalt Ferrite Oxides and Their Doped into Peg-20000

Preparation, Characterization And Magnetism Of Nanometer Cobalt Ferrite Oxide Doped La3+ And Conductivity Of Peg-20000 Compounds

Selective-precursor reducing route to cobalt nanocrystals and ferromagnetic property

Solvothermal synthesis of single-crystalline hexagonal cobalt nanofibers with high coercivity

Preparation and Megnetic Performance Study of One Dimensional Co-Ni Nanomaterial

Synthesis and Characterization of Metallic Co with Different Hierarchical Structures Prepared by A Simple Solvothermal Method

Experimental investigations and micromagnetic simulations of hybrid CoCr2O4/Ni coaxial nanostructures.

Fabrication and Magnetic Properties of Cobalt Microcrystals

Preparation of Cobalt- based Fine Alloy Powders and Magnetic Properties

Versatile fabrication of dendritic cobalt microstructures using CTAB in high alkali media

Effect of Size Distribution on Magnetic Properties in Cobalt Nanowires

A Magnetic-Field-Assisted Solution-Phase Route To Cobalt Thin Film Composed Of Cobalt Nanosheets

Study on the Microstructure and Magnetic Properties of Nd-Fe-B/Fe-Co Composite Nanowires

Preparation, Structure, and Magnetic Properties of Cobalt Nanoparticles in Carbon Fibers