Erbium-doped fluoro-sulfo-phosphate high-gain laser fiber
Yongbao Xiao,Ludong Kuang,Weichao Wang,Yao Ji,Qinyuan Zhang,Zhonghong Jiang
DOI: https://doi.org/10.1360/tb-2021-1171
2022-01-01
Chinese Science Bulletin
Abstract:Fiber lasers (FLs) with excellent beam quality, high reliability and compact structure are urgently demanded in the fields of national security and scientific research, such as high-power laser, free-space optical communication, and gravitational wave detection. These applications rely on rare-earth-doped high-gain glass fibers, which play critical roles in FLs. However, the rare earth solubility of commercial silica glass (similar to 10(19) ions/cm(3)) is restricted by its rigid structures. Thus, the active fiber fabricated by silica glass typically has low gain, which becomes a challenge for developing high-performance FLs. Phosphate-based glass is a promising candidate because it has higher solubility of rare earth (similar to 10(21) ions/cm(3)) and larger emission cross-section compared with silica glass. By incorporating fluoride and sulfate into phosphate matrix, the fluoro-sulfo-phosphate (FSP) glass that combines the favorable spectroscopic properties of fluoride and sulfate glasses with the advantages of phosphate glass can be derived. The addition of fluoride reduces the linear and nonlinear refractive indices of phosphate glass, which is advantageous for operating FLs. The maximum phonon energies of fluoride (similar to 500 cm(-1)) and sulfate (similar to 990 cm(-1)) are lower than that of phosphate (similar to 1200 cm(-1)). Therefore. sulfate and fluoride ions can tailor the local structures of rare earth and enhance radiative transition probability, leading to increased optical gain. Herein, this work systemically investigated the FSP glasses with the compositions of R2SO4-AlF3-RPO3/Zn(PO3)(2) (R=Li. Na. K). Their glass-forming regions were determined under the guidance of thermodynamic calculation method. The dependence of properties on structure of the FSP glass was analyzed by solid-state nuclear magnetic resonance (NMR). Raman spectra, differential scanning calorimetry (DSC), durability test. etc. Then the luminescent properties of Er3+/Yb3+ co-doped FSP laser glasses were characterized. Optimized laser glass was fabricated into high-gain fibers and an FL has been demonstrated. The results illustrate that the glass-forming regions of FSP systems can be quickly determined based on the thermodynamic calculation. which provides an effective and predictive method for designing novel laser glasses. Incorporating Zn(PO3)(2) into FSP glass can enhance the interactions between cations and anions and increase the polymerization degree of glass structure, resulting in improved anti-crystallization ability and chemical durability, which is beneficial for preparing large-scale samples and drawing fibers. The Er3+/Yb3+ co-doped FSP laser glasses show excellent spectroscopic properties at similar to 1.5 mu M, which exhibit longer lifetime (5.9-7.5 ms), larger emission cross section (8.5 x10(-21) 9.0 x10(-21) cm(2)) and lower saturation intensity (1.0 x10(7) W m(-2)) than some phosphate, fluorophosphate and telluroborate laser glasses. Er3+/Yb3+ co-doped fiber based on FSP glass shows a net gain of 4.7 dB/cm@1535 nm. An FL with a threshold of similar to 50 mW and a slope efficiency of 11.3% has been demonstrated based on such fiber. Considering its high gain characteristics. the narrow-line-width single-frequency FL and high-repetition-rate ultrafast FL are expected to be realized further.