Erbium-Ytterbium Co-Doped Fiber and Its Amplification Characteristics in L-Band
He Le,Yin Xiaoke,Chen Yang,Chu Yingbo,Li Jinyan
DOI: https://doi.org/10.3788/cjl231428
2024-01-01
Chinese Journal of Lasers
Abstract:Objective In the Internet of Everything era,with the rapid development of the fifth generation mobile communication technology(5G),the traffic demand in current optical communication systems shows a rapid growth trend.However,the transmission capacity in the C-band,which is the conventional band,is insufficient to satisfy continuous requirements.Exploring new bandwidths is considered the most direct and effective solution for achieving capacity enhancement.Erbium-doped fiber(EDF)amplifiers,which are commonly used to compensate for losses,play a crucial role in achieving ultra-wideband,super-large capacity,and ultralong-distance transmission.These amplifiers rely heavily on EDF,which have prompted extensive research to realize an efficient broadband amplification performance.However,most reported EDFs utilize a core-pumping scheme that relies on low electro-optical efficiency and expensive single-mode laser diodes(LD).If the multimode pumped fiber,adopting multimode LD with high electro-optical efficiency and cost-effectiveness,performs comparably with existing commercial single-mode pumped fiber,then researching multimode pumped EDF provides a feasible method to expand the bandwidth and increase the transmission capacity. Methods A cladding-pumping scheme using a multimode LD,known for its high power,has been extensively utilized in high-power fiber lasers.However,in the realm of fiber amplifiers for communication systems,the cladding-pumping scheme encounters the challenge of low optical pump efficiency owing to low pumping absorption.To address this issue,ytterbium is introduced into the EDF as a sensitizer to cross-relax with erbium,which enhances the pumping rate of erbium ions.Furthermore,phosphor-silicate glass is adopted to further inhibit the back-energy transfer from erbium to ytterbium and suppress the signal excited-state absorption.Using modeling based on the power propagation and rate equations,the doping ratio of ytterbium and erbium ions is optimized and verified to enhance the amplification performance.Considering that a higher erbium concentration may lead to clustering,which negatively affects the amplification performance of the fiber,the simulation ratio range of the ytterbium and erbium ions is set from 25∶1to 40∶1.Furthermore,erbium-ytterbium co-doped phosphor-silicate fibers are fabricated using a modified chemical vapor deposition process combined with solution doping technology.The doping concentrations of ytterbium and erbium ions are measured using an electron probe microanalyzer,which shows good agreement between the simulated optimization and experimental preparation.Furthermore,the basic parameters of the fibers are tested.Additionally,a cladding-pumping erbium-ytterbium co-doped fiber amplifier is fabricated using a commercial 940-nm multimode LD.Based on the experimental setup,the amplification performance and power consumption are evaluated and compared with those of previously reported single-mode pumped fibers. Results and Discussions The optimization criterion for the fiber length in the simulation is set as the fiber length corresponding to the highest flat gain at various doping ratios of ytterbium and erbium ions.As shown in Fig.2,as the doping ratio decreases,the gain of the fibers over the entire wavelength range increases.Simultaneously,the noise figure(NF)increases,and the noise deteriorates.Therefore,the doping ratio is optimized to 26∶1-30∶1 to obtain a trade-off between the gain and NF.Simulations are conducted to evaluate the gain variations with a pump wavelength of 940 nm,and results at signal wavelengths of 1580,1600,and 1620 nm are shown in Fig.3(a).The maximum gain efficiency at 1620 nm is calculated as 33.6 dB/W,confirming the amplification advantage of the fiber at long wavelengths at this doping ratio.Furthermore,the 940-nm multimode pump LD shows an insensitivity to pump wavelength drift with gain fluctuation＜0.3 dB,indicating a potential reduction in power consumption introduced via cooling equipment and mandatory temperature control.The amplification performance of the fabricated erbium-ytterbium co-doped phosphor-silicate fiber is evaluated based on the experimental setup with the cladding-pumping scheme.The gain and NF spectra are shown in Fig.6.With a signal power of-15 dBm covering 1565-1630 nm and a 940-nm pump power of 3 W,an average gain of 31.5 dB is obtained.At 1625 nm,the gain is 22.9 dB and NF is～5.2 dB.Furthermore,a 20 dB gain bandwidth covering 1565-1625 nm(60 nm)is achieved.In contrast,conventional single-mode pumped EDFs need at least 2 W of pump power to achieve a＞20 dB gain bandwidth up to 1625 nm.The electro-optical efficiencies of typical 980 nm and 1480 nm single-mode LDs are 12％and 6％,respectively,meaning that driving a 2 W pump power requires～16.7 W and～33.3 W electrical powers,respectively.However,this study utilizes a commercial 940 nm multimode LD with an electro-optical efficiency of 52％.Hence,only～5.8 W electrical power is necessary to drive a 3 W pump power.This approach reduces power consumption by at least 65％when compared to that of common single-mode pumped EDFs.These findings support the conclusion that enhancing multimode-pumped erbium-ytterbium co-doped fibers offers an effective method for achieving efficient broadband amplification. Conclusions In this study,an erbium-ytterbium co-doped fiber is prepared via a modified chemical vapor deposition process.The doping ratio of erbium and ytterbium ions to enhance the amplification performance is optimized and verified by numerical simulations.Based on the experimental setup,the fiber exhibits 20 dB gain bandwidth covering 1565-1625 nm,with a signal power of-15 dBm and pump power of 3 W.Furthermore,the superiority of the pump scheme using 940 nm multimode is confirmed in terms of electro-optical efficiency and temperature stability.