Monodispersed colloidal spheres for uniform y2O 3:Eu3+ red-phosphor particles and greatly enhanced luminescence by simultaneous Gd3+ doping

Ji-Guang Li,Xiaodong Li,Xudong Sun,Takamasa Ishigaki
DOI: https://doi.org/10.1021/jp802383a
2008-01-01
Abstract:Uniform red-phosphor spheres (similar to 60-300 nm in diameter) of Y2O3:Eu3+ binary and (Y,Gd)(2)O-3:Eu3+ ternary systems exhibiting excellent emission at 610 nm have been converted from their colloidal precursor spheres synthesized via homogeneous precipitation. The precursor spheres (approximate composition: [(Y1-xGdx)(1-y)-Eu-y](OH)CO3 center dot 1.3H(2)O, x = 0-0.5 and y = 0-0.11) are directly solid solutions, but arising from sequential nucleation each of the spheres has more Gd and especially ELL while having less Y going from the particle surface to the core. Eu3+ is more effective than Gd3+ in raising nucleation density, leading to rapidly decreased average size of the precursor particles at a higher Eu3+ addition. Diminishing the concentration gradients through adequate annealing is identified to be crucial to high luminous intensity of the oxide particles. At the optimal annealing temperature of 1000 degrees C, cation homogenization is achieved and the oxide particles largely retain their precursor morphologies, yielding dispersed uniform spheres of excellent luminescence. The (Y1-x-Eu-x)O-1.5 phosphor particles exhibit typical red emissions at 610 nm upon UV excitation into the charge transfer band at similar to 255 nm, and the quenching concentration of Eu3+ is found to be similar to 5 at. %. Partially replacing Y3+ with Gd3+ (up to 50 at. %) while keeping Eu3+ at the optimal content of similar to 5 at. % linearly improves the 610 nm emission, and the phosphor particles of [(Y0.5Gd0.5)(0.95)Eu-0.05]O-1.5 exhibit an luminous intensity similar to 103% of that of a commercially available Y2O3:Eu red phosphor. The uniform phosphor spheres obtained in this work are expected to have wide applications in high-resolution display technologies of contemporary interest.
What problem does this paper attempt to address?