High Quantum Yield Gd 4.67 Si 3 O 13 :Eu 3+ Red-Emitting Phosphor for Tunable White Light-Emitting Devices Driven by UV or Blue LED

Wanggui Ye,Chong Zhao,Xiaofei Shen,Chaoyang Ma,Zhonghua Deng,Yanbin Li,Yuzhen Wang,Chuandong Zuo,Zicheng Wen,Yingkui Li,Xuanyi Yuan,Chong Wang,Yongge Cao

DOI: https://doi.org/10.1021/acsaelm.1c00012

IF: 4.494

2021-03-14

ACS Applied Electronic Materials

Abstract:Eu³⁺-activated oxide components appear as a kind of rare-earth red phosphors that can be used for warm white light-emitting diode (LEDs). At present, it is still a challenge to synthesize oxide-component phosphors with high photoluminescence quantum yields compared to those of nitride and fluoride red phosphors. Herein, we propose a kind of Eu³⁺-activated Gd_4.67Si₃O₁₃ rare-earth silicate phosphor by the convenient high-temperature solid reaction method. These designed phosphors can be effectively excited by either 394 nm near-ultraviolet light or 465 nm blue light and then emit red light at a dominant wavelength of 615 nm. Particularly, for the optimal Eu³⁺-concentration-activated Gd_3.67EuSi₃O₁₃ phosphor, photoluminescence quantum yields are measured to be above 80%, which is superior to that of the general rare-earth oxide salt phosphor and comparable to that of commercial rare-earth nitride red phosphors such as Ca-α-SiAlON:Eu²⁺ (QY = 70.5%) and CaAlSiN₃:Ce³⁺ (QY = 80%). Packaged with commercial yellow phosphor Ce³⁺:YAG and UV or blue LED chip, our red component serves to improve the CRI and CCT for the tunable white light-emitting devices. Moreover, the phosphor has good thermal cycling stability with a thermal-quenching activation energy of 0.28912 eV. Finally, the temperature-dependent properties make the Gd_4.67Si₃O₁₃:Eu³⁺ phosphors have potential application in optical temperature measurement systems. The maximum relative sensitivity <i>S</i>_r is found to be 1.05 × 10^–2 K^–1 at 456 K.This article has not yet been cited by other publications.

materials science, multidisciplinary,engineering, electrical & electronic

What problem does this paper attempt to address?

The paper aims to address the current challenges of red phosphors in achieving high quantum yield. Specifically, it proposes a novel europium (Eu³⁺)-activated rare-earth silicate phosphor Gd₄.₆₇Si₃O₁₃:Eu³⁺, prepared by high-temperature solid-state reaction. This phosphor emits red light with a main wavelength of 615 nm under 394 nm near-ultraviolet or 465 nm blue light excitation, and has a high photoluminescence quantum yield of over 80%. Additionally, the phosphor exhibits good thermal cycling stability and temperature dependence, making it potentially valuable for applications in tunable white light-emitting devices and optical temperature measurement systems.

### Main Issues of the Paper:
1. **Synthesis of High Quantum Yield Red Phosphors**: Currently, synthesizing oxide component phosphors with high photoluminescence quantum yield remains a challenge, especially compared to nitride and fluoride red phosphors. The paper proposes a new europium-activated rare-earth silicate phosphor Gd₄.₆₇Si₃O₁₃:Eu³⁺, prepared by high-temperature solid-state reaction.
2. **Performance Optimization**: By optimizing the doping concentration of europium, a photoluminescence quantum yield of up to 89.2% (394 nm excitation) and 82.1% (465 nm excitation) was achieved, superior to general rare-earth oxide phosphors and close to commercial Ca-α-SiAlON:Eu²⁺ (QY = 70.5%) and CaAlSiN₃:Ce³⁺ (QY = 80%).
3. **Application Potential**: The phosphor not only performs well in tunable white light-emitting devices but also has good thermal cycling stability and temperature sensitivity, making it suitable for optical temperature measurement systems.

### Main Contributions:
- **High Quantum Yield**: The preparation of red phosphors with high photoluminescence quantum yield addresses the current shortcomings of oxide phosphors in terms of quantum yield.
- **Simple Manufacturing Process**: The use of high-temperature solid-state reaction offers a simple, cost-effective, and non-toxic process suitable for large-scale production.
- **Multiple Application Scenarios**: The phosphor is not only suitable for tunable white light-emitting devices but also has temperature sensitivity, making it applicable for optical temperature measurement systems.

I hope this information helps you understand the content of the paper! If you have more questions or need further interpretation, please feel free to let me know.