Improved Electrochemical Performance of NiO–La0.45Ce0.55O2−δ Composite Anodes for IT-SOFC Through the Introduction of a La0.45Ce0.55O2−δ Interlayer

Xiaodong Zhu,Kening Sun,Shiru Le,Naiqing Zhang,Qiang Fu,Xinbing Chen,Yixing Yuan

DOI: https://doi.org/10.1016/j.electacta.2008.03.060

IF: 6.6

2008-01-01

Electrochimica Acta

Abstract:A La0.45Ce0.55O2−δ (LDC45) interlayer between the Ni–LDC45 anode and the La0.9Sr0.1Ga0.8Mg0.2O3−δ (LSGM) electrolyte of a solid oxide fuel cell (SOFC) can prevent the solid-state reaction between Ni and LSGM. The D50 of LDC45 powders prepared via co-precipitation method was 1.36μm and the particles size distribution of LDC45 powders was rather narrow. Applying the results of an extensive investigation of screen-printing technique, a sufficiently thin and sufficiently dense LDC45 interlayer was fabricated via screen-printing using a PTFE scraper, a screen of 260mesh, and CMC as the paste binder. Additionally, an investigation of the sintering process revealed that the properties of the LDC45 interlayer can be significantly improved by sintering at 1400°C for 3h. The EIS results demonstrated that the implementation of the LDC45 interlayer in SOFC electrodes decreased their ohmic resistance and accelerated the charge transfer process. Moreover, the maximum power density of the cells was also increased 72% in this manner.