Abstract:The synthesis of Dysprosium (Dy3+) doped cobalt ferrite nanoparticles CoFe2-xDyxO4 (x=0.00, 0.02, 0.04, 0.06, 0.08) via solgel auto-combustion route was introduced. To improve the grinding process of the synthesized nano-powders, a new grinding technique (ultrasonic wet-grinding) was applied alongside the traditional grinding technique (manual dry-grinding), and the effects on the structural, morphological, and magnetic properties were investigated. The formation of face centered cubic spinel ferrite was confirmed by X-ray diffraction studies. The crystallites size was decreased with increasing Dy3+ concentration. Bulk density is increased considerably by ∼150 % and porosity is decreased by ∼11% due to ultrasonic wet-grinding technique for sample when x=0.06. Transmission Electron Microscopy and Scanning Electron Microscopy were used to study the morphological properties. The Dy3+ doping and ultrasonic-grinding technique also resulted in a narrower grain size distribution. Pureness and the presence of constituent elements Co, Fe, Dy, and O were confirmed by energy dispersive X-ray spectra. Due to sonication, the Dy weight percent increased by 78.26 % for (x=0.04). The two dominant absorption bands (υ1 and υ2) in FTIR spectra are related to tetrahedral and octahedral sites, respectively. The value of υ1 and υ2 for manual dry-grinded powders was almost stable while they fluctuated for ultrasonic wet-grinded powders. A Vibrating Sample Magnetometer (VSM) was used to examine the magnetic properties at room temperature. The maximum coercivity obtained in manual dry-grinded powder when (x=0.02) and the minimum saturation magnetization obtained in ultrasonic wet-grinded powder when (x=0.08).

Synthesis and magnetic properties of Y3-xDyxFe5O12 nanoparticles

Synthesis and magnetic properties of Sm–Y3Fe5O12 nanoparticles

Preparation and Magnetic Properties of Y3Fe5O12 Nanoparticles Doped with the Gadolinium Oxide

Magnetic properties of Nd-Y 3 Fe 5 O 12 nanoparticles

Magnetic properties of Nd-Y<sub>3</sub>Fe<sub>5</sub>O<sub>12</sub> nanoparticles

Magnetic Properties of Bi-doped Y3Fe5O12 Nanoparticles

The Origin of Enhanced Magnetodielectric Effect in Y3-xYbxFe5O12 Ceramics

The Preparation and Magnetic Properties of GdxBiY2−xFe5O12 Nanoparticles

The Synthesis and the Magnetic Properties of Sm X BiY2–x Fe5O12 Nanoparticles

Effect of lanthanum ions on magnetic properties of Y 3 Fe 5 O 12 nanoparticles

Magnetic Properties of Ce,Gd-substituted Yttrium Iron Garnet Ferrite Powders Fabricated Using a Sol–gel Method

Saturation magnetic properties of Y 3− x Re x Fe 5 O 12 (Re: Gd, Dy, Nd, Sm and La) nanoparticles grown by a sol–gel method

Fabrication and Magnetic Investigation of Y or Gd Containing CoFe2O4 Nanocrystalline Films

Synthesis of dysprosium doped cobalt ferrites nanoparticles by solgel auto-combustion method and influence of grinding techniques on structural, Morphological, and magnetic properties

Magnetic Properties of Y3Fe5O12 Nanoparticles Doped Bi and Ce Ions

Effect of Chromium on Magnetic Properties of Y2.9Ce0.1Fe5–x Cr X O12 Nanoparticles

Magnetic properties of YIG doped with cerium and gadolinium ions

Comparative Study on Doping Effects in Bi1−xDyxFe1−yMnyO3 Nanoparticles Fabricated by Sol-Gel Technique

Hydrothermal Synthesis and Ferrimagnetism of Nd3-Xsrxfe5o12(0.2 <= X <= 0.8) Substituted Garnets

Influence of Doping on the Magnetic Properties and Local Microstructures in Fe-Doped YMnO3

The magnetic properties of Ni0.7Mn0.3GdxFe2−xO4 ferrite