Dendrite growth and grain “coarsening” in an undercooled CoNi equiatomic alloy
Jianbao Zhang,Yachan Zhang,Fan Zhang,Dexu Cui,Yiming Zhao,Hongxing Wu,Xianzong Wang,Qing Zhou,Haifeng Wang
DOI: https://doi.org/10.1016/j.jallcom.2019.152529
IF: 6.2
2020-03-01
Journal of Alloys and Compounds
Abstract:The CoNi equiatomic alloy was undercooled and spontaneously solidified using the glass fluxing method. The dendrite growth behaviors were recorded by a high-speed high-resolution camera. Three dendrite growth stages (i.e., the power law growth stage when undercooling ΔT<120 K, the plateau growth stage when 120 K<ΔT<135 K and the linear law growth stage when ΔT>135 K) were found and well predicted by a dendrite growth model. For the as-solidified microstructures, the average grain size increases with undercooling, indicating that unique grain “coarsening” instead of common spontaneous grain refinement occurs. Such a grain “coarsening” phenomenon was ascribed to stress accumulation upon rapid solidification. Furthermore, a plenty of sub-grains were observed within the abnormal coarse grains. From the electron back-scattering diffraction results, the angle difference between neighbouring sub-grains was less than 6°. The current work might be helpful for not only theoretically understanding dendrite growth but also practically controlling the non-equilibrium microstructures.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering