Abstract:A novel pressurized hydrothermal post-plasma-spray process, referred to as MP-1, has been developed to convert the crystalline non-HA and amorphous components of plasma-sprayed hydroxylapatite coating back into crystalline HA. No detrimental effects are observed on the strength of either the base metal or the coating. X-ray diffraction (XRD) and FTIR analysis, surface roughness, shear adhesion strength and calcium solubility testing were conducted on Calcitite coated samples before and after treatment with this process. Other commercially available coatings were also studied using XRD and solubility testing. Quantitative XRD data show that the MP-1 treatment increases the average crystalline HA content of the Calcitite coating from 77% to 96%, while the amorphous content decreases from 21% to 4%. Other commercially available dental implant coatings ranged in crystalline HA content from 45% to 73%, with amorphous phase content ranging from 29% to 62%. FTIR spectra for treated coatings were significantly more well defined, and showed an increase in peak separation and intensity. Surface roughness and shear adhesion strength were not affected by the treatment. In vitro solubility testing revealed that for all coatings there is an initial introduction of calcium into solution over the first 2 h of testing; however, the amount of calcium dissolved was significantly lower for the MP-1 coating. Under a pH and temperature representative of normal physiologic conditions, the rate of calcium dissolution for the MP-1 coating was significantly lower than that of the other commercial HA coatings. In increasingly acidic conditions, the MP-1 coating was compared to the Calcitite coating and was found to have a significantly slower rate of calcium release. The MP-1 treatment enhances typical HA coatings by increasing the crystalline HA content at the expense of the plasma-spray-induced soluble phases without a reduction in the strength of the coating. The resulting coatings exhibit significantly decreased in vitro solubility over a wide range of pH. The results of this solubility testing suggest that the treated coating may show significantly enhanced in vivo stability, even under the extreme conditions encountered during periods of infection or rigorous detoxification procedures. The significant differences between plasma-sprayed HA coatings reported here underscore the need for industry and academic researchers to raise the level of discourse and understanding of HA coatings. By offering consistent and accurate descriptions of coating compositions and methods of analysis, meaningful comparisons between different HA coatings can be made.

Electric polarized post treatment of plasma sprayed hydroxyapatite coatings in alkaline solution

Synthesis and Characterization of Zn-substituted Hydroxyapatite Coatings by Electrochemical Deposition

Effect of EDTA on Electrodeposition of Hydroxyapatite Coatings

Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate

In vitro characterization of postheat-treated plasma-sprayed hydroxyapatite coatings

Effect of sprayed techniques on the surface microstructure and in vitro behavior of nano-HAp coatings

Effects of Hydrogen Peroxide Concentration and Heat Treatment on the Mechanical Characteristics and Corrosion Resistance of Hydroxyapatite Coatings

Immersion Behavior of Plasma-Sprayed Modified Hydroxyapatite Coatings after Heat Treatment

Impact of post-heat-treatment on the surface-roughness, residual stresses, and micromorphology characteristics of plasma-sprayed pure hydroxyapatite and 7%-Aloxite reinforced hydroxyapatite coatings deposited on titanium alloy-based biomedical implants

Significance of in-situ dry-ice blasting on the microstructure, crystallinity and bonding strength of plasma-sprayed hydroxyapatite coatings

Effect of hydrothermal treatment temperature on the hydroxyapatite coatings deposited by electrochemical method

Processing and in vitro behavior of hydroxyapatite coatings prepared by electrostatic spray assisted vapor deposition method

Effect of Heat Treatment on Characteristics of Plasma Sprayed Hydroxyapatite Coatings

Hydroxyapatite-coated Ti-6Al-4V part 2: the effects of post-deposition heat treatment at low temperatures

Characterization of Porous Titanium-Hydroxyapatite Composite Biological Coating on Polyetheretherketone (PEEK) by Vacuum Plasma Spraying

Effect of Heat Treatment of Nano-Hydroxyapatite Coatings Prepared Using Electrohydrodynamic Deposition

Hydroxyapatite Coating with Strong (002) Crystallographic Texture Deposited by Micro-Plasma Spraying

Highly crystalline MP-1 hydroxylapatite coating. Part I: In vitro characterization and comparison to other plasma-sprayed hydroxylapatite coatings

RETRACTED:Microhardness and Corrosion Behavior of Surface Gradient Oxide Coating on the Titanium Alloy Strips under High Energy Electro-Pulsing Treatment

Characteristics of Hydroxyapatite-Modified Coatings Based on TiO2 Obtained by Plasma Electrolytic Oxidation and Electrophoretic Deposition

Recent advances in multifunctional hydroxyapatite coating by electrochemical deposition