Abstract:In this paper, the influences of Cr3C2/VC content on WC grain size, WC grain shape and mechanical properties of WC–6 wt. % Co cemented carbides were investigated. The results showed that the grain size first rapidly decreased and then slightly decreased with the increasing Cr3C2/VC content, and VC led to finer grain size and narrower size distribution. HRTEM/EDS analysis of the WC/Co interface indicates that the segregation concentration of V is much larger than that of Cr, which may be a strong response to the higher inhibition efficiency of VC. The addition of Cr3C2 induced triangular prism shape WC grains while VC generated stepped triangular prism grains. Despite the grain growth inhibitor (GGI) mechanisms of Cr3C2/VC have been extensively studied in the literature, the doping amount, especially the doping limit, has not been systematically investigated. In this work, the saturated solubilities of Cr and V in cobalt binder phase along with carbon content hare been predicted based on thermodynamic calculations. Based on the theoretical calculations, the doping amount of Cr3C2/VC is designed to be gradually increasing until more or less over their maximum solubilities in the binder phase, thereby investigating the subsequent microstructure and mechanical properties. When the doping of Cr3C2/VC exceeds the maximum solubility in Co phase, Co-rich Cr-carbides and Co-deficient V-carbides would form respectively, which were detrimental to the transverse rupture strength (TRS) and impact toughness. The hardness increased with the increasing Cr3C2/VC content, while the fracture toughness decreased with the increasing Cr3C2/VC content. The TRS initially enhanced and then declined, but the stepped triangular prism shape grains and low fraction of WC/Co interface in WC–6Co–VC cemented carbide led to a more pronounced decline in the TRS. The sample with 0.6 wt. % Cr3C2 addition had good comprehensive mechanical properties, its hardness, fracture toughness and TRS were 1880 kg/mm2, 9.32 MPa·m1/2 and 3450 MPa, respectively.

Influence and function of inhibitor VC/Cr3C2 on the grain growth in super fine WC-Co cermets

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Influence of Cr3C2 and VC Content on WC Grain Size, WC Shape and Mechanical Properties of WC–6.0 wt. % Co Cemented Carbides

Effects of Cr3C2, VC, and TaC on Microstructure, WC Morphology and Mechanical Properties of Ultrafine WC–10 wt. % Co Cemented Carbides

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

Microstructural study on the grain growth inhibition of VC-doped WC-Co cemented carbides

Double Inhibitory Actions on WC Grains of Microwave Sintered WC-12wt%Co-VC Alloy

Microstructure and properties of ultrafine WC–Co–VC cemented carbides with different Co contents

Effect of Cold Isostatic Pressing and VC Grain Growth Inhibitor Addition on WC Grain Size and Mechanical Properties of WC-8Co Cemented Carbide

Effects of Lower Cobalt Binder Concentrations in Sintering of Tungsten Carbide

WC-VC/Cr3C2 composite powders prepared by a carbothermic reduction-carburization process

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Effect of carbon content on the microstructure and properties of Cr-doped WC–15Co cemented carbide

TEM and ToF-SIMS studies on the corrosion behavior of vanadium and chromium containing WC–Co hard metals in alkaline solutions

Ti(C,N)-based cermets containing uniformly dispersed ultrafine rimless grains: Effect of VC additions on the microstructure and mechanical properties

Enhancement of the mechanical properties of ultrafine-grained WC-Co cemented carbides via the in-situ generation of VC

Effects of nanocomposite grain growth inhibitors and multi-walled carbon nanotubes on the microstructure and mechanical properties of ultrafine cemented carbides

Coprecipitation of co and La 2 O 3 coprecipitation on WC for tailoring the grain distribution and boundary of high-performance coarse-grained WC-10Co cemented carbide

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Microstructure Evolution in the Cemented Carbides Wc-Coi. Effect of the C/W Ratio on the Morphology and Defects of the Wc Grains

Enhanced high temperature mechanical properties of WC-Co cemented carbides by VC addition