Abstract:Objective: The objective of the present study was to investigate the feasibility and reliability of sintering alumina and zirconia-based all-ceramic materials through a recently introduced microwave heating technique. The variation of crystal phases, the growth of grain sizes and microstructural features of these materials were evaluated after sintering. Methods: Four different groups of powder (l00%Al2O3, 60%Al2O3+40%ZrO2, 40% Al2O3+60%ZrO2, 100% ZrO2) were respectively press-compacted to fabricate green disk samples, 5 specimen of each group were prepared. All the samples were surrounded by refractory materials for heat containment and processed at 1 600 degrees C in a domestic microwave oven (850 W, 2 450 MHz), 1 600 degrees C/5 min for heating rate, 10 min for holding time. After sintering, the phase composition and average grain size of these ceramics were examined using X-ray diffraction (XRD). Their microstructure characteristics were studied by scanning electron microscopy (SEM). Results: All the specimens were successfully sintered with the application of microwave heating system in combination with a suitable thermal insulator. No phase change was found in alumina while monoclinic-zirconia was found to be transformed to tetragonal-zirconia. A little grain size growth of Al2O3 and ZrO2 has been observed with Al2O3 24.1 nm/before and 51.8 nm/after; ZrO2 25.3 nm/before and 29.7 nm/after. The SEM photos indicated that the microwave-sintered Al2O3-ZrO2 ceramics had a uniform crystal distribution and their crystal sizes could be maintained within the range of nanometers. Conclusion: It is expected that in the near future microwave heating system could be a promising substitute for conventional processing methods due to its unparalled advantages, including more rapid heating rate, shortened sintering time, superfine grain size, improved microstructure and much less expensive equipment.

Microwave Synthesis of Beta-Sialon

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Microwave synthesis process for ZSM-11 molecular sieve

[Microwave sintering of nanometer powder of alumina and zirconia-based dental ceramics]

Microwave heating and mechanism for seed-induced synthesis of SiC

Microwave Synthesis Inorganic Nanoscale Materials

STUDY ON SYNTHESIS OF MESOPOROUS MOLECULAR SIEVE MCM-41 Ⅱ. Microwave Synthesis Method

Solid-state NMR Characterization of Β-Sialons from Self-Propagating High-Temperature Synthesis

Zero‐Waste Progress for the Synthesis of High‐Purity β‐Sialon Ceramics from Secondary Aluminum Dross

Preparation of zeolite A membranes by microwave heating

Preparation of spherical α‐Al 2 O 3 nanoparticles by microwave hydrothermal synthesis and addition of nano‐Al seeds

A Novel Approach To Prepare Beta-Zeolite/Mcm-41 Composite Molecular Sieve With High Hydrothermal Stability

Fabrication of Al‐Si Alloys by Microwave Sintering

Microstructure and phase transformation behavior of Al2O3–ZrO2 under microwave sintering

Microwave Synthesis Of Nanocrystalline Metal Sulfides In Formaldehyde Solution

Synthesis and crystal morphology control of AlPO4-5 molecular sieves by microwave irradiation

Microwave synthesis of zeolites and their related applications

Preparation of SiC ceramics reinforced with in-situ generated mullite by microwave sintering

Microwave preparation of molecular sieve AlPO4-5 with nanometer sizes

Densification and grain growth of alumina by microwave processing

Microwave Sintering of Alumina at 915 MHz: Modeling, Process Control, and Microstructure Distribution