Abstract:Ammonium aluminum carbonate hydroxide (AACH) was prepared by a precipitation-azeotropic distillation method, which uses aluminum sulfate as the Al source and ammonium carbonate as the precipitant. Then, AACH was calcined into ultrafine α-Al2O3 powder. The factors that influence the dispersion property of ultrafine α-Al2O3 powder are discussed in this paper, such as the methods of adding materials, surfactant, and drying methods. The changes of the structure and property of ultrafine alumina in the thermal treatment process are also studied. The morphological structure and properties of AACH are characterized by DTA/TGA, SEM, XRD, and ICP measurements. The results show that ultrafine α-Al2O3 powder with a uniform particle size and well-distributed property can be synthesized only after aluminum sulfate atomizes into ammonium carbonate, proper amount of PEG1000 is added as the dispersant, and the product is treated by azeotropic distillation. The phase transformation of alumina during the calcination process can be described as amorphous Al2O3→γ-Al2O3→ϑ-Al2O3→α-Al2O3. The crystal grain size and density of ultrafine alumina powder increase with the increase of the calcination temperature. After AACH has been calcined at 1200°C for 2 h, the ultrafine α-Al2O3 with uniform particle size, spherical shape, and more than 99.97% purity is obtained and its powder is well dispersed.

Effects of Drying Method on Preparation of Nanometer Α-Al 2 O 3

Influence of Ammonium Chloride on Preparation of Α-Al2o3 Nanopowder by Thermal Decomposition of Ammonium Aluminum Carbonate Hydroxide

Preparation of Ultrafine Α -Al 2 O 3 Using Precipitation-Azeotropic Distillation Method

Preparation of Ultrafine Α-Al_2o_3 Using Improved Organic Solvent-drive-water Method

Study on the Synthesis of Nano Ammonium Aluminum Carbonate Hydroxide (AACH)

Research on the Prevention of Agglomeration in the Preparation of Nano-alumina by Chemical Precipitation

Spray-Drying of Alumina Powder for Aps: Effect of Slurry Properties and Drying Conditions Upon Particle Size and Morphology of Feedstock

Preparation of nanoscale alpha-Al2O3 powders by the polyacrylamide gel method

Preparation of Ultrafine Α-Al2o3 Powders by Thermal Decomposition of AACH

Preparation of Nanoscale α-Al2O3 powders by the Polyacrylamide Gel Method

Fabrication of Ultrafine Α-Al2o3 Powders by Thermal Decomposition of AACH

An Experimental Study on the Preparation of Ultrafine Flake Α-Al2o3

Study on Drying Stage of Nanoscale Powder Preparation

Effect of Drying Conditions on Crystallinity of Amylose Nanoparticles Prepared by Nanoprecipitation

PREPARATION OF NANOMETER Al_2O_3 PARTICLES

Preparation of Disperse Cake-like Α-Al2o3 Powder by AACH Method

Study on drying stage of nanoscale powder

Future Application of the Preparation Al_2O_3 Nanometer by Hydrothermal Method

The Effect of Different Heating Modes for Ammonium Aluminium Carbonate Hydroxide on the Synthesis of Α-Al2o3 Nanopowders

Controllable Preparation Conditions of Monodisperse γ-Al2O3 Nanoparticles

Preparation of monodispersed α-Al_2_O_3 nanoparticles by polymer network method with high temperature carbon isolation phase