Effects of Temperature and Holding Time on Elevated-Temperature Mechanical Properties of Aluminum Alloy 2519A

ZHANG Xin-ming,LIU Bo,LIU Ying,LI Hui-zhong,LI Hui-jie

DOI: https://doi.org/10.3321/j.issn:1004-0609.2007.10.001

2007-01-01

Abstract:The elevated-temperature mechanical properties of aluminum alloy 2519A annealed at different temperatures and different holding times were investigated by tensile test,scanning electron microscopy(SEM) and transmission electron microscopy(TEM).The results showed that for the holding time of 10 min,with increasing of temperature from room temperature to 400 ℃,the ultimate tensile strength descended from 471 MPa to 55.5 MPa,the yield strength from 440.3 MPa to 50.3 MPa,and the elongation rised from 11.6% to 21.3%.At 300 ℃,with the prolongation of holding time,the ultimate tensile strength descended from 171.6 MPa to 151.4 MPa and the yield strength from 139.4 MPa to 130.5 MPa,and then they had no remarkable changes after 1 h.At high temperatures,the decrease of the mechanical properties of the studied alloy was due to coarsening and transformation of the precipitates.