Abstract:The fatigue S-N curves of Ti-6Al-4V alloys with the bimodal and basketweave microstructures were determined between 10(5)-10(9) cyc using the ultrasonic fatigue testing system under a loading frequency of 20 kHz. The fracture surfaces of specimens were investigated with SEM. The results show that the S-N curves of Ti-6Al-4V with two kinds of microstructures continue to decrease with increasing the number of cycles and have no horizontal asymptote in the regime of 10(5)-10(9) cyc, so no conventional fatigue limits exist for Ti-6Al-4V with the two microstructures. SEM analysis shows that the crack initiation sites change from the surface to interior of specimens with decreasing the load amplitude, and therefore formed a bimodal failure distribution. The fatigue lifetime is higher under the frequency of 20 kHz as compared with that under the frequency of 25 Hz. Especially, the fatigue behavior of the basketweave microstructure shows more pronounced frequency effect than that of bimodal microstructure.

Ultra-High Cycle Fatigue Behavior of Ti-6al-4v Alloy