Preparation of ATO-Coated Conductive Fiber

Wu Jian-qing,Yan Dong-liang,Wang Yong-qing,Lu Zhen-ya

DOI: https://doi.org/10.3321/j.issn:1000-565x.2007.08.014

2007-01-01

Abstract:Conductive fiber was prepared by coating a layer of antimony-doped tin dioxide (ATO) on the surface of mullite fiber via the co-precipitation method. The influence of the preparation process on the electric resistivity and the color of the prepared conductive fiber was then investigated. The results show that (1) after heat treatment at 600 to 1000°C, the conductive fiber is of a resistivity less than 50 Ω·cm, which is almost the same as that of the ATO prepared in the same conditions; (2) when the heating temperature is higher than 1000°C, the resistivity of the conductive fiber abruptly decreases due to the compensative effect resulting from the entry of a part of Al 3+ into the SnO 2 lattice; (3) the lightness L* of the conductive fiber is higher than that of the ATO prepared at the same temperature, with a difference being more than 10 units; and (4) the chromatic aberration ΔE between the conductive fiber and the standard barium sulfate sample is less than 10 NIBS.