Electrochemical Behaviors of Phosphated/Molybdate Post-Sealed Hot-Dipped Galvanized Steel Sheet

Bi-lan Lin,Jin-tang Lu,Gang Kong

DOI: https://doi.org/10.3321/j.issn:1000-565x.2007.08.019

2007-01-01

Abstract:The hot-dipped galvanized (HDG) steel sheet was phosphated and then post-sealed using molybdate solution. Also, the corrosion performances and electrochemical behaviors of the phosphated/molybdate post-sealed HDG steel sheet in 5% NaCl solution were investigated, using Tafel polarization and electrochemical impedance spectroscopy (EIS) measurements. The results were finally compared with those of the steel sheet only with phosphating process. It is found that, after the post-sealing of the phosphated HDG samples with molybdate solution, the anodic and cathodic processes of the zinc corrosion are conspicuously suppressed, the corrosion protection efficiency markedly increases, and the electrochemical impedance increases by more than one order of magnitude. All this reveals a synergistic effect of the corrosion resistances of the phosphate coatings and the molybdate films. It is also found that the low-frequency diffusion impedance increases with the immersion time at the initial stage of immersion in 5% NaCl solution, which demonstrates clearly the self-repairing capability of the composite coatings.