Effect of Impurities Pinning on the Domains of PSTZT Ceramics

Wei Shi,Qiang Chen,Lin Chen,Wei Huang,Yi Zhao,Dingquan Xiao,Jianguo Zhu

DOI: https://doi.org/10.1109/isaf.2007.4393265

2007-01-01

Abstract:(1-x)Pb(Sc0.5Ta0.5)O3-xPb(Zr0.52Ti0.48)O-3 (PSTZT-100x) ceramics were prepared by using conventional oxide processing, and their piezoelectric and ferroelectric properties studied. The results of X-ray diffraction (XRD) suggest that PSTZT-100x ceramics formed a single-phase perovskite structure when 0.1=x=0.8. The ceramics exhibit relatively good piezoelectric and ferroelectric properties: piezoelectric constant, d(33)=117 pC/N; planar electromechanical coupling factor, k(p) = 45%, remnant polarization, P-r=14 mu C/cm(2), coercive field, E-c=0.65 kV/mm. When x>0.70, the polarization-field hysteresis curves of PSTZT ceramics show "pinched" shapes instead of the normal square-like P-E loops when tested at room temperature and different frequency. In the meantime, the coercive field, polarization and internal bias field of PSTZT ceramics are strongly dependent on frequency or temperature. A defect pinning may induces the unsaturated hysteresis loop of PSTZT ceramics.