Abstract:A minor amount of CO2 in air usually causes a detrimental effect on oxygen activation over a solid oxide fuel cell (SOFC) cathode because insulating surface carbonate is easily formed, which inhibits charge transfer during the oxygen reduction reaction (ORR). In this study, we report that the detrimental effect due to the CO2 interaction with perovskite oxide can be turned into a beneficial effect for facilitating ORR through tailoring the material composition of the perovskite. More specifically, for cobalt-free SrSc0.025Nb0.075Fe0.9O3-δ (SSNF), the exposure to the CO2 atmosphere results in the formation of a minor amount of surface strontium carbonate mainly in the form of a nanofilm over the perovskite surface, which protects the electrode from further corrosion by CO2, thus achieving a relatively stable performance even under a 10% CO2-containing air atmosphere. When CO2-free air is restored, the SrCO3 is successfully decomposed at intermediate temperatures. As a result, the surface reaction kinetics is recovered to the initial degree while the charge transfer process is obviously improved. An area-specific resistance of only 0.07 Ω cm2 is achieved at 650 °C after the CO2-induced surface activation, much smaller than the original value of 0.13 Ω cm2. In addition, the CO2-treated electrode shows a fairly stable performance for ORR under a subsequent CO2-free air atmosphere. To create such a beneficial effect, it is critical to tailor the degree of interaction of the perovskite surface with CO2, while the benchmark Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCF) shows a too strong interaction with CO2 with the formation of bulk-phase-like carbonate, which failed to decomposed even when restored with a CO2-free atmosphere at intermediate temperatures, and as a result, worsened the ORR activity after the CO2 treatment.

Significant impact of nitric acid treatment on the cathode performance of Ba0.5Sr0.5Co0.8Fe0.2O3-δ perovskite oxide via combined EDTA-citric complexing process

Evaluation of A-site deficient Sr1−xSc0.175Nb0.025Co0.8O3−δ (x=0, 0.02, 0.05 and 0.1) perovskite cathodes for intermediate-temperature solid oxide fuel cells

Properties and Performance of Ba0.5Sr0.5Co0.8Fe0.2O3−δ + Sm0.2Ce0.8O1.9 Composite Cathode

Spectrum and performance of Pr0.6-xNdxSr 0.4FeO3-δ cathode

A Novel Route to Synthesize Nano-Crystalline Ba0.5sr0.5co0.8fe0.2o3-Delta Perovskite Oxide at High Temperature

Suppressing the Surface Amorphization of Ba0.5Sr0.5Co0.8Fe0.2O3-δ Perovskite toward Oxygen Catalytic Reactions by Introducing the Compressive Stress

Tuning Ba0.5Sr0.5Co0.8Fe0.2O3-δ cathode to high stability and activity via Ce-doping for ceramic fuel cells

BaCO3 Nanoparticles-Modified Composite Cathode with Improved Electrochemical Oxygen Reduction Kinetics for High-Performing Ceramic Fuel Cells

Effect of octahedral occupancy of bimetal-doping and CO 2 -induced surface reconstruction on oxygen reduction reaction of cobalt-based perovskite oxides

Spectrum And Performance Of Pr(0.6-X)Ndxsr(0.4)Feo(3-Delta) Cathode

Properties of composite cathodes composed of Pr3+-deficient perovskite oxide and ionic conductor Ce0.8Sm0.2O1.9

Effect of HNO3 treatment on the La0.6Sr0.4Co0.2Fe0.8O3-delta obtained via combined EDTA-citrate complexing process

Developing an ultrafine Ba0.5Sr0.5Co0.8Fe0.2O3-δ cathode for efficient solid oxide fuel cells

Effect of A-site Deficiency in BaCe0.8Sm0.2O3-δ on the Electrode Performance for Proton Conducting Solid Oxide Fuel Cells

Toward Enhanced Oxygen Evolution on Perovskite Oxides Synthesized from Different Approaches: A Case Study of Ba0.5Sr0.5Co0.8Fe0.2O3−δ

Preparation and properties of BaxSr1-xCoyFe1-yO3-δ cathode material for intermediate temperature solid oxide fuel cells

Effect of HNO3 treatment on the La0.6Sr0.4Co0.2 Fe0.8O3-δ obtained via combined EDTA-citrate complexing process

Turning Detrimental Effect into Benefits: Enhanced Oxygen Reduction Reaction Activity of Cobalt-Free Perovskites at Intermediate Temperature via CO2-Induced Surface Activation

Promotional role of BaCO3 on the chromium–tolerance of La0.6Sr0.4Co0.2Fe0.8O3-δ cathodes of solid oxide fuel cells

Manipulating Electrocatalytic Activity of Perovskite Oxide Through Electrochemical Treatment

Enhanced Electrochemical Performance of Ba0.5Sr0.5Co0.8Fe0.2O3-δ Cathode by Zr4+, Sm3+ and Yb3+ Tri-Doped BaCeO3 Compositing for Intermediate-Temperature Thin-Film Fuel Cells