Properties of composite cathodes composed of Pr3+-deficient perovskite oxide and ionic conductor Ce0.8Sm0.2O1.9

Asim Idrees,Xuening Jiang,Lei Jiang,Qingyu Zhang

DOI: https://doi.org/10.1016/j.ceramint.2020.04.051

IF: 5.532

2020-08-01

Ceramics International

Abstract:Cathode is a key factor that determines performance of solid oxide fuel cells (SOFCs). Here, new composite materials based on Pr3+-deficient double-layered perovskite oxide Pr0.95BaCo2O6-δ and Ce0.8Sm0.2O1.9, marked as P0.95BCO-xSDC (x = 0, 30, 40, 50 wt%) were synthesized. Thermal expansion coefficient of the composite cathodes decreases with the higher SDC content. Addition of SDC was found to decrease total electrical conductivities of the cathode but enhance its catalytic activity over oxygen reduction reaction (ORR). Area specific resistance (ASR) of the cathodes first decreases from x = 0 to x = 40 wt% and then slightly increase at x = 50 wt%. Addition of SDC could promote ionic transfer process across the cathode/electrolyte interface, leading to small ASRs at low temperatures for the composite cathodes. Among the studied samples, the x = 40 wt% cathode exhibited the highest ORR catalytic activity characteristic of the lowest ASR values ranging from 0.005 Ω cm2 at 750 °C to 0.288 Ω cm2 at 500 °C with Ea of 1.02eV. An anode supported single cell was fabricated based on the x = 40 wt% cathode, and high peak powder densities, such as 1171 mW cm−2 at 750 °C and 917 mW cm−2 at 700 °C were achieved, further demonstrating its high ORR catalytic activity as a promising cathode material.

materials science, ceramics