Abstract:In this paper, the physicochemical properties and cytotoxicity of calcium phosphate cement (CPC), prepared by mixing cement powders of tetracalcium phosphate (TTCP) and dicalcium phosphate (DCPA) with a cement liquid of physiological saline solution, were investigated. The microstructure evolution of various hardened cement bodies and their hydration crystals as a function of immersion time in similar physiological fluids, physiological saline solution (0.9% NaCl), or simulated body fluids (SBF), were also studied. Results show that the setting time of CPC is in the range of 12-15 min, which meets the clinical application demands. We also found that the mean compressive strength of the CPC samples immersed in SBF for 3 days is 104 +/- 10 MPa which reaches the transverse compressive strength, 106-133 MPa, of human long bone. The results obtained from both the X-ray powder diffraction analyses (XRD) and scanning electron microscopy (SEM) observations indicated that a reinforcing effect of some remaining TTCP particles in the early stages of immersion is mainly responsible for the increase in the initial strength. Although the CPC failed to keep this high level when immersed for a longer time, the initial reinforcing effect of the remaining TTCP particles provides advantages for clinical applications. This would be effective when the material is loaded at the very beginning of the implantation, especially for the material used as a fixation, which requires a certain initial strength in the early stages of the implantation. The cytotoxicity results showed that the relative growth rate (RGR%) of L929 cells on the CPC samples using physiological saline solution as a cement liquid was slightly Superior to that of the samples using the 0.5 mol/L phosphate acid solution as the cement liquid. This was most likely caused by the pH difference between the two CPC samples immersed in a DMEM-BFS medium. (c) 2006 Wiley Periodicals, Inc.

Thermokinetic Analysis of the Hydration Process of Calcium Phosphate Cement

The exothermal behavior in the hydration process of calcium phosphate cement.

Mechanisms of hydration of calcium phosphate cement

Rheological properties of calcium phosphate cement during the hydration process

Calorimetric Study of Magnesium Potassium Phosphate Cement

Control of crystallinity of hydrated products in a calcium phosphate bone cement.

Control of Crystallinity of Hydrated Products in a Calcium Phosphate Cement

Morphological and phase characterizations of retrieved calcium phosphate cement implants

Development of calcium phosphate cement and analysis

Hydration Mechanism of a Novel PCCP + DCPA Cement System

Preparation of Hydroxyapatite Cement and Analysis As of Its Disposition

The physicochemical properties of the solidification of calcium phosphate cement.

Effects of the Composition of the Bioactive Composite Calcium Phosphate Cement on Its Behavior in the Solution

A method for determining the hydration degree of magnesium potassium phosphate cements

Effect of K+ Diffusion on Hydration of Magnesium Potassium Phosphate Cement with Different Mg/P Ratios: Experiments and Molecular Dynamics Simulation Calculations

The Effect of the Thermosensitive Biodegradable PLGA–PEG–PLGA Copolymer on the Rheological, Structural and Mechanical Properties of Thixotropic Self-Hardening Tricalcium Phosphate Cement

Solution Property of Calcium Phosphate Cement Hardening Body

Thermodynamic study on the phase assemblage of MPC exposed to natural and accelerated carbonation conditions

Physicochemical properties of TTCP/DCPA system cement formed in physiological saline solution and its cytotoxicity.

Effect of biomedical organic compounds on the setting reaction of calcium phosphates.

Fabrication of a glycerol-citrate polymer coated tricalcium phosphate bone cements: Structural investigation and material properties