Abstract:The corrosion-induced failure of marine reinforced concrete structures, stemming from prolonged exposure to environments with elevated chloride content, poses a significant threat to structural integrity and serviceability. Traditional models predominantly depend on prior information to estimate the spatial stochastic degradation of aging structures, leading to a lack of comprehensiveness and accuracy in evaluation results. To address these limitations, a data-driven probabilistic assessment model for corrosion failure is proposed. This model incorporates a pre-training phase that integrates electrochemical simulations with long-term exposure data to establish the spatiotemporal distribution of corrosion failures, thereby facilitating a thorough assessment of overall damage by quantifying the corrosion failure proportion while propagating epistemic uncertainty. Subsequently, a multivariate function is derived using the non-dominated sorting genetic algorithm to elucidate the relationship between input and output variables. The efficacy of the data-driven model is evaluated through experimental observations and model predictions. The Hangzhou Bay Bridge project serves as a case study, wherein this model is demonstrated using actual data obtained from exposure experiments and field detection. Furthermore, the proposed model enables a rapid prejudgment of corrosion failure proportion, significantly reducing diagnostic time compared to conventional procedures.

Dynamic Simulation Method for Probability Evolution of Reinforcement Steel Corrosion

A Probabilistic Model For Corrosion Prediction Of Steel Reinforcement

Probability-Based Performance Degradation Model and Constitutive Model for the Buckling Behavior of Corroded Steel Bars

Corrosion-crack path based probabilistic model to predict the durability behavior of RC components

Path probability model of corrosion-crack assessment for existing reinforced concrete structures

Probabilistic Approach for Durability Design of Concrete Structures in Marine Environments

Probabilistic Lifetime Assessment of Marine Reinforced Concrete with Steel Corrosion and Cover Cracking

Probability Analysis Of Corrosion Process Of Corroded Rc Flexural Member In Marine Environment

Simulation Analysis for Probability Density of Buried Pipeline's Area Corrosion Ratio

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

Reinforcement Corrosion-Induced Cover Cracking and Its Time Prediction for Reinforced Concrete Structures

Service Life Prediction of Precast Concrete Structures Exposed to Chloride Environment

Time-dependent reliability analysis of reinforced concrete beams subjected to bending and marine atmospheric environment

Influence of Stochastic Chlorine Environment on the Spatiotemporal Deterioration of Marine RC Structures

Probabilistic constitutive model for corroded structural steel with stochastic pits under monotonic tension

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Stochastic Characteristics of Reinforcement Corrosion in Concrete Beams under Sustained Loads

Time-dependent seismic fragility analysis of reinforced concrete columns subjected to chloride-induced corrosion

Probability of Corrosion Failure Analysis Using an Adaptive Sampling Approach

Failure Probability Analysis of Corroded RC Structures Considering the Effect of Spatial Variability

Durability degradation simulation of RC structure based on gamma process considering two-dimensional chloride diffusion and life probabilistic prediction