Chemical grafting of Co 9 S 8 onto C 60 for hydrogen spillover and storage
Lu Han,Wei Qin,Jia Zhou,Jiahuang Jian,Songtao Lu,Xiaohong Wu,Guohua Fan,Peng Gao,Boyu Liu
DOI: https://doi.org/10.1039/c7nr00581d
IF: 6.7
2017-01-01
Nanoscale
Abstract:Metal modified C<sub>60</sub> is considered to be a potential hydrogen storage medium due to its high theoretical capacity. Research interest is growing in various hybrid inorganic compounds-C<sub>60</sub>. While the design and synthesis of a novel hybrid inorganic compound-C<sub>60</sub> is difficult to attain, it has been theorized that the atomic hydrogen could transfer from the inorganic compound to the adjacent C<sub>60</sub> surfaces via spillover and surface diffusion. Here, as a proof of concept experiment, we graft Co<sub>9</sub>S<sub>8</sub> onto C<sub>60</sub>via a facile high energy ball milling process. The Raman, XPS, XRD, TEM, HTEM and EELS measurements have been conducted to evaluate the composition and structure of the pizza-like hybrid material. In addition, the electrochemical measurements and calculated results demonstrate that the chemical "bridges" (C-S bonds) between these two materials enhance the binding strength and, hence, facilitate the hydriding reaction of C<sub>60</sub> during the hydrogen storage process. As a result, an increased hydrogen storage capacity of 4.03 wt% is achieved, along with a favorable cycling stability of ∼80% after 50 cycles. Excluding the direct hydrogen storage contribution from Co<sub>9</sub>S<sub>8</sub> in the hybrid paper, the hydrogen storage ability of C<sub>60</sub> was enhanced by 5.9× through the hydriding reaction caused by the Co<sub>9</sub>S<sub>8</sub> modifier. Based on these experimental measurements and theoretical calculations, the unique chemical structure reported here could potentially inspire other C<sub>60</sub>-based advanced hybrids.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry