Abstract:We report the preparation of ordered porous carbons for the first time via nanocasting zeolite 10X with an aim to evaluate their potential application for hydrogen storage. The synthesized carbons exhibit large Brunauer-Emmett-Teller surface areas in the 1300-3331 m(2)/g range and pore volumes up to 1.94 cm(3)/g with a pore size centered at 1.2 nm. The effects of different synthesis processes with pyrolysis temperature varied in the 600-800 °C range on the surface areas, and pore structures of carbons were explored. During the carbonization process, carbons derived from the liquid-gas two-step routes at around 700 °C are nongraphitic and retain the particle morphology of 10X zeolite, whereas the higher pyrolysis temperature results in some graphitic domains and hollow-shell morphologies. In contrast, carbons derived from the direct acetylene infiltration process have some incident nanoribbon or nanofiber morphologies. A considerable hydrogen storage capacity of 6.1 wt % at 77 K and 20 bar was attained for the carbon with the surface area up to 3331 m(2)/g, one of the top-ranked capacities ever observed for large surface area adsorbents, demonstrating their potential uses for compacting gaseous fuels of hydrogen. The hydrogen capacity is comparable to those of previously reported values on other kinds of carbon-based materials and highly dependent on the surface area and micropore volume of carbons related to the optimum pore size, therefore providing guidance for the further search of nanoporous materials for hydrogen storage.

Ordered Micro-Porous Carbon Molecular Sieves Containing Well-Dispersed Platinum Nanoparticles for Hydrogen Storage

HYDROGEN ADSORPTION IN ORDERED MESOPOROUS CARBON SYNTHESIZED BY A SOFT-TEMPLATE APPROACH

Large Surface Area Ordered Porous Carbons Via Nanocasting Zeolite 10X and High Performance for Hydrogen Storage Application.

Micro-channel Development and Hydrogen Adsorption Properties in Templated Microporous Carbons Containing Platinum Nanoparticles

Hydrogen Storage in Several Metal‐phosphate Molecular Sieves

Ordered Porous Carbon with Tailored Pore Size for Electrochemical Hydrogen Storage Application

Engineering the Electronic Structure of Platinum Single-Atom Sites via Tailored Porous Carbon Nanofibers for Large-Scale Hydrogen Production

Performance Characterization and Comparison Study of Silver Molecular Sieve Hydrogen Adsorbents in Liquid Hydrogen Vessels

Nanoporous adsorbents for hydrogen storage

Preparation of sulfur-doped microporous carbons for the storage of hydrogen and carbon dioxide

Nanoporous Ni with High Surface Area for Potential Hydrogen Storage Application

Modification of as Synthesized SBA-15 with Pt nanoparticles: Nanoconfinement Effects Give a Boost for Hydrogen Storage at Room Temperature

Ultrafine Pt nanoparticles anchored on core–shell structured zeolite–carbon for efficient catalysis of hydrogen generation

Platinum Atoms and Nanoparticles Embedded Porous Carbons for Hydrogen Evolution Reaction

Effect of Pt nanoparticle decoration on the H2 storage performance of plasma-derived nanoporous graphene

High Efficiency Graphitized Carbon Coated Pt Composite for Hydrogen Electro-Oxidation and Hydrogen Storage

On the Nature of Spillover Hydrogen Species on Platinum/nitrogen-Doped Mesoporous Carbon Composites: A Temperature-Programmed Nitrobenzene Desorption Study

Understanding platinum-based H2 adsorption/ desorption kinetics during catalytic hydrogenation or hydrogen storage-related reactions

High surface area microporous carbon materials for cryogenic hydrogen storage synthesized using new template-based and activation-based approaches

High-Performance Hydrogen Storage Nanoparticles Inside Hierarchical Porous Carbon Nanofibers with Stable Cycling.

Platinum-Decorated Graphene: Experimental Insight into Growth Mechanisms and Hydrogen Adsorption Properties